Product description:
LOCTITE SI 5145 is specifically formulated for bonding, sealing, and coating of electronic devices, especially for military, automotive and industrial electronic. The non-slumping nature of this product makes it ideal for reinforcing and strain relieving delicate components. LOCTITE SI 5145 resists weathering, moisture, ozone and retains its properities through severe environments. This product is typically used in applications up to 200 °C. Further information on the product can be obtained from the local technical department:

Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. Use LOCTITE SF 7063.
2. Full performance properties will develop over 72 hours.
3. Moisture curing begins immediately after the product is exposed to the atmosphere, therefore parts to be assembled should be mated within a few minutes after the product is dispensed.
4. Excess material can be easily wiped away with non-polar solvents.

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Typical properties of no-cured material
  • Specific gravity in temperature 25°C : 1,10
  • Content of non-volatile substances : 92
Typical properties of cured material
Cured in a relative humidity of 50% for 1 week at temperature 21-26°C
  • Tensile strength, ASTM D 412, N/mm² : 3,40
  • Elongation, ASTM D 412, % : 500
  • Hardness, ASTM D 2240, Shore'a A : 25
  • Water absorption, ASTM D 570, 24 hours at room temperature : 0,01 %

Full technical information can be found in the technical data sheet.