TEROSON WX 400 - 1L (wax for closed profiles) /Terotex HV 400 Extra
No.
IDH.784176
Price
Associated products:
TEROSON WX 400 - 1L (wax for closed profiles) /Terotex HV 400 Extra
Associated products:
Product description:
TEROSON WX 400 is a solvent containing anticorrosive agent for cavity conservation with high solids, based on waxes, polymers and anticorrosive additives. The material is a thixotropic solution which can be well atomized. This leads to optimum protection even of those areas which are difficult to reach and also between narrow sheet metal tolerances. TEROSON WX 400 infiltrates and displaces humidity. The product contains a high content of corrosion inhibitors. TEROSON WX 400 atomizes to a fine fog during spraying, has excellent penetration characteristics, penetrates well into the gaps to be protected (e.g. welding seams), but does not run off significantly from lower seams. The material may also be applied at temperatures starting at 10°C, but penetration is improved when product and car body have normal room temperature. After complete drying TEROSON WX 400 forms a plastic, water-repellent film with a beige transparent colour. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Application:
Pocessing with the can:
TEROSON WX 400 can be applied, with the HV Cup Pistol with the respective probes. Application pressure for the HV Cup Pistol is 2 - 4 bar. Do not spray onto rubber parts! After a longer storage period as well as at temperatures below 10°C the material builds up a certain thixotropy. However, this is broken during spraying procedure - the material, therefore, exhibits its normal characteristics after application. Depending on the cavity to be treated the drying period can last up to several days; assure sufficient ventilation during drying.
Cleaning:
TEROSON WX 400 drips can easily be wiped off. For cleaning dried material TEROSON VR 10 is suitable; larger areas can be steam jet cleaned. Contamination on painted areas should be removed immediately
Storage:
Frost sensitive : yes Recommended storage temperature : 15 to 25 °C;Thickens at lower temperatures and must be brought to application temperature prior to use Shelf life : 24 months
Parameters:
Colour: beige transparent Odour: characteristic odour Consistency : thixotropic Density approx. : 0.96 g/cm³ Solid : approx. 60 % Dripping Temperature of the solids (DIN 51801) : approx. 150 °C Sag resistance : min. 100 µm Penetration : >55 mm; gap 0,1 mm Paint compatibility no permanent changes of the top-coat Removability after 24 hrs dried material : can easily be removed Behaviour in the repair paint oven (1.5 hrs at 90°C) : no running off Behaviour in the cold : no cracks
Full information can be found on the technical data sheet of the product.
TEROSON WX 400 is a solvent containing anticorrosive agent for cavity conservation with high solids, based on waxes, polymers and anticorrosive additives. The material is a thixotropic solution which can be well atomized. This leads to optimum protection even of those areas which are difficult to reach and also between narrow sheet metal tolerances. TEROSON WX 400 infiltrates and displaces humidity. The product contains a high content of corrosion inhibitors. TEROSON WX 400 atomizes to a fine fog during spraying, has excellent penetration characteristics, penetrates well into the gaps to be protected (e.g. welding seams), but does not run off significantly from lower seams. The material may also be applied at temperatures starting at 10°C, but penetration is improved when product and car body have normal room temperature. After complete drying TEROSON WX 400 forms a plastic, water-repellent film with a beige transparent colour. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Application:
Pocessing with the can:
TEROSON WX 400 can be applied, with the HV Cup Pistol with the respective probes. Application pressure for the HV Cup Pistol is 2 - 4 bar. Do not spray onto rubber parts! After a longer storage period as well as at temperatures below 10°C the material builds up a certain thixotropy. However, this is broken during spraying procedure - the material, therefore, exhibits its normal characteristics after application. Depending on the cavity to be treated the drying period can last up to several days; assure sufficient ventilation during drying.
Cleaning:
TEROSON WX 400 drips can easily be wiped off. For cleaning dried material TEROSON VR 10 is suitable; larger areas can be steam jet cleaned. Contamination on painted areas should be removed immediately
Storage:
Parameters:
Full information can be found on the technical data sheet of the product.