Product description:
TEROSON PU 9225 UF ME is a polyurethane based two-component adhesive which cures at room temperature. For accelerated curing itis recommended to increase the temperature up to 60 to 70 °C. The product is supplied in a convenient twin cartridge and is rapid-curing.TEROSON PU 9225 UF ME can be painted with normal commercial car repair refinishing paints. When applying TEROSON PU 9225 UFME to plastics the use of an approved Henkel primer is absolutely necessary. Detailed information see directions of use. Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
Pretreatment:
The parts to be bonded must be free from oil, grease, moisture, dirt and release agents. Pre-cleaning with a high pressure injectioncleaner is recommended. After drying the parts should be cleaned with Teroson FL+. Damaged plastic parts have to be sanded on theface side with a narrow belt sander (grit P 80 to 120) to grind a V-groove (1 to 2 cm). Finally the sanded parts should be cleaned withTeroson FL+. When applying TEROSON PU 9225 UF ME to plastics the use of primer TEROSON 150 in a thin layer is absolutely necessary. Evaporation time is approx. 10 minutes.

Application:
Insert the cartridge into a suitable application gun. Apply pressure to the cartridge(s) to ensure a simultaneous and homogeneous flow of both components. Thereafter, attach the static mixer and cut the tip to provide for the desired bead size. Discard the first 2 cm of extruded adhesive bead. TEROSON PU 9225 UF ME is applied directly to the substrates. Any excess material should be removed immediately after application. If material is left in the cartridge leave the static mixer attached. For further use of the product, simply remove the mixer and install a new one. In case of plastic repair the use of woven fibreglass mat is recommended for reinforcing.

Curing:
Curing occurs at room temperature and needs only approx. 5 to 6min. to get grindability. To get a faster grindability the parts bondedwith TEROSON PU 9225 UF ME can be warmed up to 60 to 70 °C for minimum 3 to 4 minutes.

Cleaning:
Freshly applied and uncured material should be removed with a dry cloth and then cleaned off with a suitable solvent. Cured adhesivecan only be removed with the use of a machine.

Storage:
  • Frost sensitive : no
  • Recommended storage temperature : 10 to 25 °C
  • Shelf life : 12 months

    Parameters:
    COMPONENT A:
    • Color: grey
    • Density : approx. : 1,6 g/cm³
    COMPONENT B:
    • Color : white
    • Density : approx. 1,3 g/cm³
    MIXTURE:
    • (COMPONENT A + B) (1 : 1 )
    • Color : grey
    • Potlife (23°C ) : approx. <1 minutes
    • Tack-free time : approx. 2 minutes ( 23 °C, 50 % rh)
    • Curing time in 23 °C : approx. 1,5 godz.
    • Layer thickness : 3 mm
    • Hardness, Shore A approx. : 95

    Full technical information can be found in the technical data sheet.
  • Assortment