Teroson MS 9320 SF OC - 300ml (spray mass, ochre)

Product description:
TEROSON MS 9320 SF is a sprayable sealant based on SMP-Polymer, that crosslinks to a rubber-elastic material with good abrasion resistance by absorbing humidity from the air. Skin formation time and curing time depend on humidity and temperature. In addition, the curing time also depends on the layer thickness. By increasing the temperature and humidity, the reaction time can be reduced; low temperatures as well as low humidity retard the process. TEROSON MS 9320 SF is outstanding on account of the following properties:

- Sealant and seam sealing product in one,
- High sag resistance,
- Sprayable and brushable,
- Can be applied using a flat spray nozzle or a broad jet nozzle,
- Can be painted up to three days after application with solvent-coating and water borne paint systems,
- Broad range of adhesion without the use of primer,
- Spotweldable if not completely cured,
- free of isocyanate and silicone,
- Very rapid curing,
- UV resistant,
- High ageing resistance

Further information can be obtain from local technical department: biuro@woronko-loctite.pl

Directions for use:
Pre-Treatment:
The adhesion of Terostat TEROSON MS 9320 SF is improved, if the contact surfaces (plastics) are roughened with an abrasive non-woven. The substrates must be clean, dry and grease free. For pretreatment TEROSON VR 20 is suitable. After the cleaning of ground / bare steel and aluminum surfaces we recommend a pretreatement with BONDERITE 1455-W Wipes. This improves adhesion and corrosion protection.

Processing:
For the spraying of TEROSON MS 9320 SF from cartridges, the MultiPress telescope-pistol (for spraying only!) should be used. With this pistol it is possible to apply TEROSON MS 9320 SF either in the form of a material bead (“sealant bead”) or to spray it on by means of a two-circuit air system. The PowerLine II-pistol with the appropriate nozzles must be used for reproducing the new flatstream seals, since this requires higher pressures. TEROSON MS 9320 SF can either be sprayed or brushed, i.e. with TEROSON MS 9320 SF it is possible to reproduce structural seams as well as structures obtained by means of a brush. TEROSON MS 9120 or TEROSON MS 9120 SuperFast, which are perfectly compatible with TEROSON MS 9320 SF can be used as an undercoat material. Virtually all types of structures specified by the manufacturer can be reproduced rapidly and without problems by means of appropriate adjustments of the pistols. Furthermore, it is possible to adapt the width and limitation of the seam depending on the spray distance. See the operating instructions for the adjustment and use of the pistols.

Storage:
  • Frost-Sensitive : No
  • Recommended storage temperature, °C : 10 to 25
  • Shelf-life : 12 months

    Parameters:
  • Colour : grey, ocher, black,
  • Odour : characteristic,
  • Density, g/cm³ : approx. 1.5,
  • Consistency : paste,
  • Sag resistance : very good,
  • Curing mechanism : humidity curing,
  • Cure rate, mm/24 hrs* : approx. 4.5,
  • Skin formation time, min* : 8 to 20,
  • Shore-A-hardness (DIN 53505) : approx. 30,
  • Adhesion : raw metal sheet, EC paint, top-coat paint, metallic paint,
  • Paint compatibility : Yes (see for: overpainting),
  • Chemical resistance : resistant to UV-ageing and weathering,
  • Application temperature, °C : 15 to 35,
  • In service temperature range, °C : -30 to 90,
  • Short exposure (up to 3 h), °C : 120

    Further information can be found in the technical data sheet