Teroson RB 4006 GY - 570 ml (butyl sealant)/Terostat 4006 - 570 ml

Product description:
Teroson RB 4006 is a high quality, gun-grade, one component sealant based on butyl rubber with a low solvent content. After evaporation of the solvents, Teroson RB 4006 represents a tough plastic, extrudable, deformable sealing mass. The complete drying depends on the ambient temperature and on the applied layer thickness. Due to its deformability Teroson RB 4006 should only be used for sealing of gaps with little or no movement. Teroson RB 4006 is suitable for the sealing of inner and outer joints. The product can be applied on horizontal as well as on vertical areas wihtout draining off. Further information about the product can be obtain from local technical department: biuro@woronko-loctite.pl

Application Areas:
Teroson RB 4006 is mainly used for the sealing of sheet metal and plastic overlaps i.e. in the field of caravan, motor home industry or air controlling / ventilation technology.

Directions for use:
Pre-Treatment:
The substrates must be clean, dry, oil and grease free. For cleaning we recommend Cleaner A, D and FL.

Application:
The processing of 310-ml-cartridges is carried out by a handor air pressure pistol. For compressed air pistols, a pressure of 2 to 5 bar is needed, depending on the nozzle cross section and processing speed. For the processing of Teroson RB 4006 out of hobbocks, processing equipment with extrusion pumps is needed (minimum pressure conversion 30:1).

Cleaning:
Teroson RB 4006 can be removed by knife or spatula. The remaining layer can be washed off with Cleaner FL or a cleaning solvent.

Storage:
  • Frost-Sensitive : no
  • Recommended Storage Temperature, °C : 5 to 30
  • Shelf-life (in unopened original packaging), months : 12

    Parameters:
  • Density, g/cm³ : approx. 1.4
  • Consistency : pasty
  • Solids, % : approx. 85
  • Skin formation time, min* : approx. 20 to 30 (after application)
  • Setting time, weeks : 1 to 2
  • Sag resistance : very good
  • Acceptable deformation, % : <5
  • In service temperature range, °C : -20 to 80

    Further information can be found in the technical data sheet