Product description:
LOCTITE SI 5615 is a two part, fast cure silicone with excellent bond strength to glass, metals and Ceran. LOCTITE SI 5615 has excellent hot strength up to 180 °C with the capability to resist higher temperatures for short-term exposure. Typical applications include sealing/bonding glass stovetop assemblies, weld and rivet reduction in high temperature applications, and other high temperature bonding applications. Further information on the product can be obtained from your local technical department:

Steps to achieve the best adhesive results:
1. For best performance the mating surface should be clean and free of grease. Use LOCTITE SF 7063.
2. Best results are achieved utilizing a helix 8mm diameter, 24 element mix nozzle.
3. After dispense, mate parts immediately to ensure maximum bond strength.
4. Dual Cartridges: Insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Next, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. Attach the static mixing nozzle to the end of the cartridge and begin dispensing the adhesive. Purge and dispose of the first 3 - 5 cm from the end of the mix nozzle, as it may not be sufficiently mixed. Bulk Containers: Utilize volumetric dispense system to ensure proper mix ratio and utilize mix nozzle to obtain adequate mixing.

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Shear strength, ISO 4587 (Cured for 7 days in temperature 22 °C / 50% rh) :
  • Aluminum (Alclad), N/mm² : 1,8
  • Steel (grit blasted), N/mm² : 1,7
  • Stainless steel, N/mm² : 1,8
  • Cooper, N/mm² : 1,7
  • Brass, N/mm² : 1,6
  • Polycarbonate, N/mm² : 1,5
  • PVC, N/mm² : 1,5
  • PMMA, N/mm² : 0,4
  • PET, N/mm² : 0,9
  • Nylon 66, N/mm² : 1,3
  • GRP, N/mm² : 1,7
  • Phenolic, N/mm² : 1,5
  • Wood (teak), N/mm² : 1,0
  • EPDM, N/mm²: 0,1
  • ABS, N/mm² : 0,7

Full technical information can be found in the technical data sheet.