Product description:
LOCTITE SI 5091 is used for potting, coating and sealing of various automotive, electronic, military and industrial components. Normal processing conditions will include exposure to sufficient UV light irradiance to effectively cure the material. Surface and/or atmospheric moisture will promote the cure of material in shadowed regions. Although functional strength is developed almost instantly due to the UV curing nature of LOCTITE SI 5091, increased cure properties are developed during 72 hours at ambient conditions. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. You can use LOCTITE SF 7063.
2. The product is designed to be initially cured with UV light at a minimum irradiance of 30 mW/cm2 for approximately 20 seconds, increased exposure may be required for curing deeper sections.
3. Functional strength is achieved almost instantly.
4. Full performance properties will develop over 72 hours.
5. Moisture curing begins immediately after the product is exposed to the atmosphere, therefore parts to be assembled should be mated within a few minutes after the product is dispensed.
6. Excess material can be easily wiped away with non-polar solvents.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: Storage temperature is dependent upon package size. Consult product label or Henkel Certificate of Analysis for packaged storage conditions. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
Cured at 75 mW/cm², measured at 365 nm, for 60 seconds per side plus 3 days at 22 °C / 50±5% RH :Shore Hardness, ISO 868, Durometer A : 31 to 37 Elongation, ISO 37, % : ≥75 Tensile Strength, ISO 37 N/mm² : ≥0.6
Cured at 40 mW/cm², for 60 seconds, plus 7 days post UV Cure at 22 °C / 50% RH : Lap Shear Strength, ISO 4587:
-Aluminum to Glass N/mm² : 0.01 to 0.1
-Steel to Glass N/mm² : 0.1 to 0.4
-Glass to Glass N/mm² : 0.1 to 0.6
Full technical information can be found in the technical data sheet
LOCTITE SI 5091 is used for potting, coating and sealing of various automotive, electronic, military and industrial components. Normal processing conditions will include exposure to sufficient UV light irradiance to effectively cure the material. Surface and/or atmospheric moisture will promote the cure of material in shadowed regions. Although functional strength is developed almost instantly due to the UV curing nature of LOCTITE SI 5091, increased cure properties are developed during 72 hours at ambient conditions. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. You can use LOCTITE SF 7063.
2. The product is designed to be initially cured with UV light at a minimum irradiance of 30 mW/cm2 for approximately 20 seconds, increased exposure may be required for curing deeper sections.
3. Functional strength is achieved almost instantly.
4. Full performance properties will develop over 72 hours.
5. Moisture curing begins immediately after the product is exposed to the atmosphere, therefore parts to be assembled should be mated within a few minutes after the product is dispensed.
6. Excess material can be easily wiped away with non-polar solvents.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: Storage temperature is dependent upon package size. Consult product label or Henkel Certificate of Analysis for packaged storage conditions. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
Cured at 75 mW/cm², measured at 365 nm, for 60 seconds per side plus 3 days at 22 °C / 50±5% RH :
Cured at 40 mW/cm², for 60 seconds, plus 7 days post UV Cure at 22 °C / 50% RH :
-Aluminum to Glass N/mm² : 0.01 to 0.1
-Steel to Glass N/mm² : 0.1 to 0.4
-Glass to Glass N/mm² : 0.1 to 0.6
Full technical information can be found in the technical data sheet