TEROSON PU 8597 - 570ml (window glass adhesive, fast) /Terostat 8597
No.
IDH.317767
Product description:
The direct glazing adhesive is outstanding for the following properties:
- Very good sag resistance
- High cure rate
- High elastic and shear strength, even after aging
- Good adhesion to the remaining material
- Excellent adhesion to glass, glass with the ceramic coating, encapsulation and to painted surfaces, in connection with primer/activator
- High UV resistance in connection with primer/activator
Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Priming:
With the use of an applicator apply a thin layer of All-in-one primer TEROSON PU 8519P to the cleaned substrate surface. Ensure the wet film should be 0.025 mm. Let the primed surface evaporate for approx. 2 minutes before the direct glazing sealant is applied. If a fresh bonding is made directly on the remaining material layer (left in the window cut–out of the body), this layer should not be primed within the first 2 hours after cutting back. But if the remaining layer is not used within the first 2 hours, it has to be activated with TEROSON PU 8519P. Provided that it is not contaminated with dust or grease, the remaining layer is the best adhesive surface, if TEROSON PU 8597 is used for the new bond. If windows are bonded which have been pre-coated with a primer or PUR–based adhesive/sealant by the glass supplier, the primer TEROSON PU 8519P is also suitable to ensure the correct adherence of TEROSON PU 8597 to the pre-coating. By means of an applicator, a thin layer of TEROSON PU 8519P is applied to the pre-coating. Following this, an evaporation time of approx. 15 minutes has to be observed. Subsequently, TEROSON PU 8597 is applied as usual, but taking into consideration the layer thickness of the pre-coating.
Processing:
The direct glazing sealant TEROSON PU 8597 is processed from the cartridge or foil pack using commercial equipment such as hand, battery driven or air-pressure guns with a piston rod.
Preliminary Statement:
Prior to use it is necessary to read the Safety Data Sheet for information about precautionary measures and safety recommendations. Also, for chemical products exempt from compulsory labeling, the relevant precautions should always be observed.
Storage:
Frost sensitive : no Recommended storage temperature : 5 to 25 °C Shelf life : 12 months foil pack 18 months aluminium cartridge
Parameters:
Full technical information can be found in the technical data sheet.
The direct glazing adhesive is outstanding for the following properties:
- Very good sag resistance
- High cure rate
- High elastic and shear strength, even after aging
- Good adhesion to the remaining material
- Excellent adhesion to glass, glass with the ceramic coating, encapsulation and to painted surfaces, in connection with primer/activator
- High UV resistance in connection with primer/activator
Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Priming:
With the use of an applicator apply a thin layer of All-in-one primer TEROSON PU 8519P to the cleaned substrate surface. Ensure the wet film should be 0.025 mm. Let the primed surface evaporate for approx. 2 minutes before the direct glazing sealant is applied. If a fresh bonding is made directly on the remaining material layer (left in the window cut–out of the body), this layer should not be primed within the first 2 hours after cutting back. But if the remaining layer is not used within the first 2 hours, it has to be activated with TEROSON PU 8519P. Provided that it is not contaminated with dust or grease, the remaining layer is the best adhesive surface, if TEROSON PU 8597 is used for the new bond. If windows are bonded which have been pre-coated with a primer or PUR–based adhesive/sealant by the glass supplier, the primer TEROSON PU 8519P is also suitable to ensure the correct adherence of TEROSON PU 8597 to the pre-coating. By means of an applicator, a thin layer of TEROSON PU 8519P is applied to the pre-coating. Following this, an evaporation time of approx. 15 minutes has to be observed. Subsequently, TEROSON PU 8597 is applied as usual, but taking into consideration the layer thickness of the pre-coating.
Processing:
The direct glazing sealant TEROSON PU 8597 is processed from the cartridge or foil pack using commercial equipment such as hand, battery driven or air-pressure guns with a piston rod.
Preliminary Statement:
Prior to use it is necessary to read the Safety Data Sheet for information about precautionary measures and safety recommendations. Also, for chemical products exempt from compulsory labeling, the relevant precautions should always be observed.
Storage:
Parameters:
- Color: black
- Odor: weak
- Consistency: thick, non-dripping paste
- Density: approx. 1,2 g/cm3
- Solid: 100 %
- Curing method: under the influence of moisture
- Curing speed: approx. 5 mm/24 h (23°C, 50% wilg.)- DIN 50014
- Hardness Shore'a A: approx. 55 ( DIN 53505 )
- Tensile strength: approx. 8,5 MPa ( DIN 53504 )
- The modulus of transverse elasticity: approx. 1,2 Mpa ( DIN 54451 )
- Elongation at break: approx. 300 % ( DIN 53504 )
- Tensile strength: 2,0 MPa ( after 24 hours; DIN 50014 )
Full technical information can be found in the technical data sheet.