Product description:
LOCTITE AA V5004 is a structural acrylic adhesive that provides toughness and excellent adhesion to plastics, metals and composites. The cured product is virtually transparent making it well suited for bonding applications requiring clear, invisible glue lines. LOCTITE AA V5004 has very high shear strength and resistance to peel, fatigue, and impact loads. This product will adhere to a wide variety of surfaces including most structural thermoplastics, thermosets, FRP, stone, ceramics, steel and aluminum. LOCTITE AA V5004 is useful to join dissimilar materials. Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
FOR ASSEMBLY:
1. For high strength structural bonds, remove surface contaminants such as paint, oxide films, oils, dust, mold release agents and all other surface contaminants. You can use for example LOCTITE SF 7063.
2. Use gloves to minimize skin contact. DO NOT use solvents for cleaning hands.
3. Dual Cartridges:
Insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Next, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. Attach the static mixing nozzle to the end of the cartridge and begin dispensing the adhesive. Purge and dispose of the first 3 - 5 cm from the end of the mix nozzle, as it may not be sufficiently mixed.
Bulk Containers:
Utilize volumetric dispense system to ensure proper mix ratio and utilize mix nozzle to obtain adequate mixing.
4. For maximum bond strength apply adhesive evenly to both surfaces to be joined.
5. Application to the substrates should be made as soon as possible. Larger quantities and/or higher temperatures will reduce the working time.
6. Join the adhesive coated surfaces and allow to cure. Higher temperatures will speed up curing.
7. Keep assembled parts from moving during cure. The bond should be allowed to develop full strength before subjecting to any service load.

FOR CLEAN UP:
1. Uncured material may be cleaned from dispenser components and surfaces with a variety of solvents; including LOCTITE SF 7063, LOCTITE Equipment Flushing Solvent, IPA, acetone, MEK, methylene chloride, etc.
2. Removal of material that has been mixed should be done quickly as polymerization occurs rapidly.
3. After use, the static mixer may be used in place of the cap.
4. When the product is reused, a new static mixer must be used.
5. Contact your equipment supplier to ensure that any solvents used are compatible with individual components.

Storage:
Store product in the unopened container in a dry location. Material removed from containers may be contaminated during use. Do not return liquid to original container.
Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Henkel cannot assume responsibility for product which has been contaminated or stored under conditions other than those recommended.

Parameters:
Shear strength, ISO 4587 (cured for 168 hours in 22 °C):
  • PVC, N/mm² : 9
  • Stainless steel, N/mm² : 16
  • Aluminum (etched), N/mm² : 13
  • ABS, N/mm² : 7,5
  • Carbon steel (shot-blasted), N/mm² : 22,5
  • Polycarbonate, N/mm² : 4
  • PMMA, N/mm² : 7
  • Galvanized steel, N/mm² : 13
  • FRP, N/mm² : 5,6
  • Composit coating, N/mm² : 12

Full technical information can be found in the technical data sheet.