TEROSON RB 53 SPECIAL - 1,4kg (Sealing compound) / Terolan 53 Spezial

TEROSON RB 53 SPECIAL - 1,4kg (Sealing compound) / Terolan 53 Spezial (IDH.2671595)

Product description:
TEROSON RB 53 is a solvent containing, brushable sealant based on styrene-butadiene rubber with high sag resistance. With the enclosed brush it is possible to reproduce the factory texture of the surface. TEROSON RB 53 is a high solid system with slight change in volume. As a result of this the brush texture will be nearly completly preserved. TEROSON RB 53 exhibits good adhesion to bare, galvanized, primed and painted steel sheets, as well as to rigid PVC. After drying TEROSON RB 53 can be overpainted with all standard automotive paints (conventional and waterbased). Due to the manifold paint systems existing in the market preliminary tests should always be carried out. Further information about the product: biuro@woronko-kleje.pl

APPLICATION AREAS:
TEROSON RB 53 is particularly used for sealing overlap joints. It is mainly used in workshops were a brush texture will be reproduced like the factory texture during the application.

Directions for use:
Pretreatment
The contact faces must be dry, clean and free from grease. Small traces of oils can be absorbed by TEROSON RB 53. Rust, forging scales and peeling layers of paints must first be removed.

Application
TEROSON RB 53 is applied from the 1 l tin with a brush. Because of the rapid evaporation of the solvents the tin must be closed immediately after use. Corrections to the brush texture are possible until skin formation occurs in; afterwards the torn skin will produce an uneven surface.

Storage:
  • Frost sensitive : no
  • Recommended storage temperature : 10 to 25 °C
  • Shelf life : 12 months in original packaging

    Parameters:
  • Colour : light green
  • Odour : smell of aromatics
  • Consistency : paste
  • Density : approx. 1.4 g/cm³
  • Solids : approx. 80 %
  • Sag resitance : good
  • Skin formation : time* 3 to 5 min
  • Full drying* : 20 to 48 hrs
    - Coating thickness : 3 mm
  • Volume change : approx. 20 %
  • Aging resistance : very good
  • In service temperature : -25 to 80 °C
  • Short exposure (up to 1h) : 150 °C

    Full technical information can be found in technical data sheet