TEROSON PU 9096 PL - 310ml (adhesive for window glass)

TEROSON PU 9096 PL - 310ml (adhesive for window glass) (IDH.1230375)

Product description:
The direct glazing adhesive is outstanding for the following properties:
- Very good sag resistance
- High cure rate
- High elastic and shear strength, even after aging
- Good adhesion to the remaining material
- Excellent primerless adhesion to glass, glass with the ceramic coating, encapsulation and to painted surfaces
- Improved UV resistance
Further information about the product: biuro@woronko-kleje.pl

Directions for use:
The substrates to be bonded must be dry and free from oil, dust, grease and other dirt. Clean new glass thoroughly with TEROSON VR 100. Check new glass if it is correct and free of any damage. To obtain an optimal adhesion we recommend abrading the windscreen’s bond line with a smooth abrasive pad in order to have a clean surface. Clean and pretreat the bonding surfaces with TEROSON VR 20 after abrading and allow to dry for 2 minutes. The layer remaining in the window cut–out need not to be cleaned. If, however, cleaning of this remaining layer is indispensable, an evaporation time of at least 5 minutes has to be observed before the sealant can be applied, since the adhesive surfaces must have fully dried.The direct glazing sealant TEROSON PU 9096 PL is processed from the cartridge using commercial equipment such as hand, battery driven or air-pressure guns.

Storage:
  • Frost sensitive : no
  • Recommended storage temperature :10 to 25 °C
  • Shelf life : 9 months in original packaging

    Parameters:
  • Colour : black
  • Odour : weak
  • Consistency : smooth, sag-resistiant, pasty
  • Density g/cm³ : approx. 1.3
  • Solids : 100 %
  • Cure rate (DIN 50014; 23°C, 50% rh) : approx. 3 to 4 mm / 24 h
  • Skin formation time (DIN 50014; 23 °C, 50% rh) : approx. 25 min.
  • Shore-A-hardness (DIN 53505) : approx. 60
  • Tensile strenght (DIN 53504) L: approx. 7.5 MPa

    Further information can found in the technical data sheet