TEROSON PU 8630 2K HMLC - 310ml (glass adhesive. Extended assembly time)
No.
IDH.794668
Files to download:
- Karta Techniczna - TEROSON PU 8630 HMLC
- Technical Data Sheet - TEROSON PU 8630 HMLC
- Technisches Datenblatt - TEROSON PU 8630 HMLC
- Karta Charakterystyki (Składnik A) - TEROSON PU 8630 HMLC
- Karta Charakterystyki (Składnik B) - TEROSON PU 8630 HMLC
- Safety Data Sheet (Component A) - TEROSON PU 8630 HMLC
- Safety Data Sheet (Component B) - TEROSON PU 8630 HMLC
- Sicherheitsdatenblatt (Komponent A) - TEROSON PU 8630 HMLC
- Sicherheitsdatenblatt (Komponent B) - TEROSON PU 8630 HMLC
TEROSON PU 8630 2K HMLC - 310ml (glass adhesive. Extended assembly time)
Product description:
The direct glazing adhesive is outstanding for the following properties:
- Very good sag resistance
- High elastic and shear strength, even after aging
- Very low conductivity
- Good adhesion to the remaining material
- High shear modulus
- High UV resistance in connection with primer/activator
- Excellent adhesion to glass, glass with the ceramic coating, encapsulation and to painted surfaces, in connection with primer/activator
- Easy to use ( application with battery gun / 1C pneumatic gun)
Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Priming:
With the use of an applicator apply a thin layer of All-in-one primer TEROSON PU 8519P to the cleaned substrate surface.Ensure the wet film should be 0.025 mm. Let the primed surface evaporate for approx. 15 minutes before the direct glazing sealant is applied. If a fresh bonding is made directly on the remaining material layer (left in the window cut–out of the body), this layer should not be primed within the first 2 hours after cutting back. But if the remaining layer is not used within the first 2 hours, it has to be activated with TEROSON PU 8519P. Provided that it is not contaminated with dust or grease, the remaining layer is the best adhesive surface, if TEROSON PU 8630 HMLC is used for the new bond. If windows are bonded which have been pre-coated with a primer or PUR–based adhesive/sealant by the glass supplier, the primer TEROSON PU 8519P is also suitable to ensure the correct adherence of TEROSON PU 8630 HMLC to the pre-coating. By means of an applicator, a thin layer of TEROSON PU 8519P is applied to the pre-coating. Following this, an evaporation time of approx. 15 minutes has to be observed. Subsequently, TEROSON PU 8630 HMLC is applied as usual, but taking into consideration the layer thickness of the pre-coating.
Processing:
Prior to its use, the cartridge containing the A-component of TEROSON PU 8630 HMLC must be warmed in the TEROSON cartridge warming box for at least 30 minutes, resp. 60 minutes in the pre-heating box for cartridges and foil packs. Immediately before the application, the B-component is fully screwed onto the opened cartridge. Then processing is carried out using a battery driven gun or a compressed-air pistol with a piston rod.
Recommeded tools:
TEROSON PoweLineII ; working pressure: 8 to 10 bar Application should be performed in one step. Extrusion time for a complete cartridge should be between 90 to 120 seconds to achieve the best performance.
Storage:
Frost sensitive yes Recommended storage temperature : 5 to 25 °C Shelf life : 12 months aluminium cartridge
Parameters:
Colour: black Odour: weak Consistency: smooth, sag-resistiant, pasty Density g/cm³: approx. 1.2 Solids: 100 % Shore-A-hardness: (DIN 53505) approx. 60 Tensile strength: (DIN 53504) approx. 9.5 MPa Stress: (DIN 53504) approx. 5.7 MPa at 100 % elongation Shear modulus: (according to DIN 54451) approx. 3.0 MPa Elongation at break: (DIN 53504) approx. 370 % Shear strength: Layer thickness 5mm based 4 to 5 MPa (fully cured)
Full technical information can be found in the technical data sheet.
The direct glazing adhesive is outstanding for the following properties:
- Very good sag resistance
- High elastic and shear strength, even after aging
- Very low conductivity
- Good adhesion to the remaining material
- High shear modulus
- High UV resistance in connection with primer/activator
- Excellent adhesion to glass, glass with the ceramic coating, encapsulation and to painted surfaces, in connection with primer/activator
- Easy to use ( application with battery gun / 1C pneumatic gun)
Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Priming:
With the use of an applicator apply a thin layer of All-in-one primer TEROSON PU 8519P to the cleaned substrate surface.Ensure the wet film should be 0.025 mm. Let the primed surface evaporate for approx. 15 minutes before the direct glazing sealant is applied. If a fresh bonding is made directly on the remaining material layer (left in the window cut–out of the body), this layer should not be primed within the first 2 hours after cutting back. But if the remaining layer is not used within the first 2 hours, it has to be activated with TEROSON PU 8519P. Provided that it is not contaminated with dust or grease, the remaining layer is the best adhesive surface, if TEROSON PU 8630 HMLC is used for the new bond. If windows are bonded which have been pre-coated with a primer or PUR–based adhesive/sealant by the glass supplier, the primer TEROSON PU 8519P is also suitable to ensure the correct adherence of TEROSON PU 8630 HMLC to the pre-coating. By means of an applicator, a thin layer of TEROSON PU 8519P is applied to the pre-coating. Following this, an evaporation time of approx. 15 minutes has to be observed. Subsequently, TEROSON PU 8630 HMLC is applied as usual, but taking into consideration the layer thickness of the pre-coating.
Processing:
Prior to its use, the cartridge containing the A-component of TEROSON PU 8630 HMLC must be warmed in the TEROSON cartridge warming box for at least 30 minutes, resp. 60 minutes in the pre-heating box for cartridges and foil packs. Immediately before the application, the B-component is fully screwed onto the opened cartridge. Then processing is carried out using a battery driven gun or a compressed-air pistol with a piston rod.
Recommeded tools:
TEROSON PoweLineII ; working pressure: 8 to 10 bar Application should be performed in one step. Extrusion time for a complete cartridge should be between 90 to 120 seconds to achieve the best performance.
Storage:
Parameters:
Full technical information can be found in the technical data sheet.