Product description:
TEROSON EP 5010 TR is a solvent free, two component, high strength levelling compound based on Epoxy Resins with low density. By heating up both components the chemical reaction will accelerate. TEROSON EP 5010 TR has been specially developed for body rework and for rebuilding of car body metal surfaces to substitute traditional tin soldering. It is free of isocyanate, silicones and lead. The product has no shrinkage and is excellent for grinding. TEROSON EP 5010 TR shows no sagging and has very good modeling properties. Further information about the product: biuro@woronko-kleje.pl

Directions for use:
TEROSON EP 5010 TR is processed from universal cartridges with manual application tools (guns driven by hand, air pressure or battery). Only use cartridge pistols that are equipped with a piston rod. Insert the cartridge into a suitable application gun. Applypressure to the cartridge to ensure a simultaneous and homogeneous flow of both components. Thereafter, clean the tip andattach the static mixer. To ensure proper mixing, discard the first approx. 5 cm of the adhesive bead. If material is left in the cartridge leave the static mixer attached. For further use of the product, simply remove the mixer and install a new one. Apply the levelling compound onto the repair area in a way that the area is sufficiently filled with excessive material. After curing excessive material is sanded back and sanding residues are removed. Thereafter clean the sanded parts with TEROSON VR 10. Further treatment (e.g. filling or painting) is executed according to the directions of the manufacturer. The use of fine filler is recommended. The material is not designed to be used on large repair areas at buses and coaches like side panels and roofs.

Storage:
  • Frost sensitive conditionally
  • Recommended storage temperature : 15 to 25 °C
  • Shelf life : 12 months in original packaging

    Parameters:
  • Colour grey
  • Odour no smell after curing
  • Potlife acc. to Bohlin (oscillating)
    -at 20 °C 90 min(s)
    - at 30 °C 60 min(s)
  • Density (cured) approx. 0.7 g/cm³
  • Water absorbtion 24 hr(s) at 98 % rh and 40 °C : <0.5 % weigth gain
  • In service temperature -40 to 90 °C

    Full technical information can be found in the technical data sheet