LOCTITE PC 7229 - 10kg (epoxy resin with fine-grained ceramic filler, to 230 °C)
No.
IDH.255895
LOCTITE PC 7229 - 10kg (epoxy resin with fine-grained ceramic filler, to 230 °C)
Product description:
Loctite 7229 Nordbak High Temperature Pneu-Wear is a small ceramic bead filled two-part epoxy putty, designed to protect equipment from fine particle abrasion. Temperature range –30° to +230°C. High Temperature Pneu-Wear requires post-curing for ultimate performance and temperature resistance.
Loctite 7229 Nordbak High Temperature Pneu-Wear is a small ceramic bead filled two-part epoxy putty, designed to protect equipment from fine particle abrasion. Temperature range –30° to +230°C. High Temperature Pneu-Wear requires post-curing for ultimate performance and temperature resistance.
Advantages
· Small ceramic bead filled – resists fine particle abrasion.
· Prolongs equipment life
· Easy to mix and use – renews worn surfaces fast, reduces downtime
· Non sag – provides abrasion resistance on over-head and vertical surfaces
TYPICAL APPLICATIONS
· Providing protective lining in pneumatic conveying systems
· Repairing and providing abrasion resistance:
- in elbows
- in exhausters
- in hoppers
- in cyclones
- In dust collectors
Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Surface Preparation
Proper surface preparation is critical to the long-term performance of this product. The exact requirements vary with the severity of the application, expected service life, and initial substrate conditions.
· Thoroughly clean and abrade surfaces (grit blast if possible), finally clean with LOCTITE SF 7063. The more thorough the degree of surface preparation the better the performance of the application.
· On vertical or overhead areas, tack welding expanded metal mesh onto the metal substrate is recommended prior to application of 7229 Pneu-Wear. Mixing:
· Measure 4 parts resin to 1 part hardener by volume or weight, transfer entire kit onto a clean and dry mixing surface and mix together until uniform in colour. (If resin and hardener temperatures are 15°C or below, preheat resin only to about 30°C but not to exceed 40 °C.
Application
· Apply fully mixed material to the prepared surface.
· Initially apply the material in a very thin layer to “wet” out the surface and avoid air entrapment.
· Build up to desired thickness (minimum 6mm), avoid air entrapment
· At 25°C, the working time is 30 minutes. Functional cure time is 6 hours, post cure at 150°C for 2 hours.
Storage:
Product shall be ideally stored in a cool, dry location in unopened containers at a temperature between 8 °C to 28 °C unless otherwise labelled. Optimal storage is at the lower half of this temperature range. To prevent contamination of unused product, do not return any material to its original container. For further specific shelf life information, contact Loctite UK Technical Service.
Parameters:
Compressive strength, ASTM D695, N/mm² : 103.4 Shear strength, ASTM D1002, N/mm² (at the gap 0.125 mm, acid-etched aluminum) : 34.5 Hardness, ASTM D-2240, Shore D : 85 Working life, minutes 30 Cure time, hours : requires post cure, see directions for use.
Full technical information can be found in the technical data sheet
· Small ceramic bead filled – resists fine particle abrasion.
· Prolongs equipment life
· Easy to mix and use – renews worn surfaces fast, reduces downtime
· Non sag – provides abrasion resistance on over-head and vertical surfaces
TYPICAL APPLICATIONS
· Providing protective lining in pneumatic conveying systems
· Repairing and providing abrasion resistance:
- in elbows
- in exhausters
- in hoppers
- in cyclones
- In dust collectors
Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Surface Preparation
Proper surface preparation is critical to the long-term performance of this product. The exact requirements vary with the severity of the application, expected service life, and initial substrate conditions.
· Thoroughly clean and abrade surfaces (grit blast if possible), finally clean with LOCTITE SF 7063. The more thorough the degree of surface preparation the better the performance of the application.
· On vertical or overhead areas, tack welding expanded metal mesh onto the metal substrate is recommended prior to application of 7229 Pneu-Wear. Mixing:
· Measure 4 parts resin to 1 part hardener by volume or weight, transfer entire kit onto a clean and dry mixing surface and mix together until uniform in colour. (If resin and hardener temperatures are 15°C or below, preheat resin only to about 30°C but not to exceed 40 °C.
Application
· Apply fully mixed material to the prepared surface.
· Initially apply the material in a very thin layer to “wet” out the surface and avoid air entrapment.
· Build up to desired thickness (minimum 6mm), avoid air entrapment
· At 25°C, the working time is 30 minutes. Functional cure time is 6 hours, post cure at 150°C for 2 hours.
Storage:
Product shall be ideally stored in a cool, dry location in unopened containers at a temperature between 8 °C to 28 °C unless otherwise labelled. Optimal storage is at the lower half of this temperature range. To prevent contamination of unused product, do not return any material to its original container. For further specific shelf life information, contact Loctite UK Technical Service.
Parameters:
Full technical information can be found in the technical data sheet