Product description:
LOCTITE 574 seals close fitting joints between rigid metal faces and flanges. The product cures when confined in theabsence of air between close fitting metal surfaces. Provides resistance to low pressures immediately after assembly of flanges. Typically used as a form-in-place gasket on rigid flanged connections, e.g. gearbox and engine casings, etc. The thixotropic nature of LOCTITE 574 reduces the migration of liquid product after application to the substrate. Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. Use LOCTITE SF 7063.
2. The product is designed for close fitting flanged parts with gaps up to 0,25 mm.
3. Apply manually as a continuous bead or by screen printing to one surface of the flanges.
4. Low pressures (<0.5 MPa) may be used when testing to confirm a complete seal immediately after assembly and before curing.
5. Flanges should be tightened as soon as possible after assembly to avoid shimming.

Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Parameters:
  • Shear strength on steel : 8,5 N/mm²
  • Time to get full strength at the gap 0,05 mm (22 °C):
    -Steel : 12 hours
    -Aluminum : 15 hours
  • Time to obtain initial strength at the gap 0,05 mm (22 °C):
    -Steel : 15 minutes
    -Aluminum : 50 minutes
  • Working temperature : from -55 °C to +150 °C
  • Color : orange


Full technical information can be found in the technical data sheet.