Product description:
LOCTITE EA 9484 is a tough, medium viscosity, industrial grade epoxy adhesive with a medium work life. Once mixed the two-part epoxy cures at room temperature to form a flexible gray bondline with excellent resistance to shock and impact. The fully cured epoxy is resistant to a wide range of chemicals and solvents, and acts as an excellent electrical insulator. LOCTITE EA 9484 is suited for low-stress, high-impact bonding applications of dissimilar materials. It can be used for repairing strain gauges, sealing seams on fiberglass components, repairing printed circuit boards, bonding stainless steel inserts, and rubber hose to steel tubing. Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
1. For best performance surfaces for bonding should be clean, dry and free of grease. You can use LOCTITE SF 7063. For high strength structuralbonds, special surface treatments can increase the bond strength and durability.
2. To use, resin and hardener must be blended. Product can be applied directly from dual cartridges by dispensing through the mixer head supplied. Discard the first 3 to 5 cm of bead dispensed. Using bulk containers, mix thoroughly by weight or volume in the proportions specified in the Product Description Matrix. For hand mixing, weigh or measure out the desired amount of resin and hardener and mix thoroughly. Mix approximately 15 seconds after uniform color is obtained.
3. Do not mix quantities greater than 500 g in mass as excessive heat build-up can occur. Mixing smaller quantities will minimize the heat build-up.
4. Apply the adhesive as quickly as possible after mixing to one surface to be joined. For maximum bond strength apply adhesive evenly to both surfaces. Parts should be assembled immediately after mixed adhesive has been applied.
5. Working life of the mixed adhesive is 40 minutes at 22 °C. Higher temperature and larger quantities will shorten this working time.
6. Keep the assembled parts from moving during cure. The joint should be allowed to develop full strength before subjecting to any service loads.
7. Excess uncured adhesive can be wiped away with organic solvent (e.g. Acetone).
8. After use and before adhesive hardens, mixing and application equipment should be cleaned with hot soapy water.

Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Parameters:
Material cured for 7 days ( temperature 22 °C ) :
  • Dielectric breakdown strength, kV/mm : 15,6
  • Tensile strength ASTM, N/mm² : 15
  • Elongation ASTM D882, % : 50
  • Tensile strength, (ASTM D882), N/mm² : 161
  • Hardness ASTM D1706, Shore D : 55
  • Glass temperature, Tg, °C 30
Shear strength at the gap 0,05 mm ( after 3 days at temperature 22 °C ) :
  • Steel (shot-blasted) : 25 N/mm²
  • Aluminum, anodized : 6,3 N/mm²
  • Aluminum, etched with iron sulphate : 6,8 N/mm²
  • Stainless steel : 13,4 N/mm²
  • Galvanized steel: 20 N/mm²
  • Polycarbonate : 3,8 N/mm²
  • Nylon : 2,6 N/mm²
  • Wood (fir) : 6,6 N/mm²
  • ABS : 4,2 N/mm²
  • GRP (polyester resin reinforced with fiberglass) : 6,2 N/mm²
  • Glass fiber reinforced epoxy : 10 N/mm²
Full technical information can be found in the product technical sheet.