Product description:
LOCTITE® EA 9466™ is a toughened, industrial grade epoxy adhesive with extended work life. Once mixed, the two component epoxy cures at room temperature to form a tough, off-white bondline which provides high peel resistance and high shear strengths. The fully cured epoxy is resistant to a wide range of chemicals and solvents, and acts as an excellent electrical insulator. LOCTITE® EA 9466™ provides excellent bond strengths to a wide variety of plastics and metals. Typical applications include general purpose industrial applications requiring extended work life for adjusting parts during assembly. Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
1. For best performance part surfaces should be clean and free of grease. You can use LOCTITE SF 7063.
2. For high strength structural bonds, remove surface contaminants such as paint, oxide films, oils, dust, mold release agents and all other surface contaminants.
3. Dual Cartridges: To use simply insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Next, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. If automatic mixing of resin and hardener is desired, attach the mixing nozzle to the end of the cartridge and begin dispensing the adhesive. For hand mixing, expel the desired amount of the adhesive and mix thoroughly. Mix for approximately 15 seconds after uniform color is obtained. Bulk Containers: Mix thoroughly by weight or volume in the proportions specified in Product Description section. Mix vigorously, approximately 15 seconds after uniform color is obtained.
4. Do not mix quantities greater than 4 kg as excessive heat build-up can occur. Mixing smaller quantities will minimise the heat build-up.
5. Apply the adhesive as quickly as possible after mixing to one surface to be joined. For maximum bond strength apply adhesive evenly to both surfaces. Parts should be assembled immediately after mixed adhesive has been applied.
6. Keep assembled parts from moving during cure. The bond should be allowed to cure 24 hours before subjecting to any service loads.
7. Excess uncured adhesive can be wiped away with organic solvent (e.g. Acetone).
8. After use and before adhesive hardens mixing and dispensing equipment should be cleaned with hot soapy water.

Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Parameters:
Resin:
- Chemical type: epoxy
- Appearance: white no-transparent paste
- Specific gravity in 25°C: 1
- Viscosity RVT wg metody Brookfielda w 25°C, mPas: 15,000 do 50,000
- Flash point (TCC), °C (°F) >93 (>200)

Hardener:
- Chemical type: amine
- Appearance: white transparent liquid
- Specific gravity in 25°C: 1
- Viscosity RVT according to the Brookfield method in 25°C, mPas: 25,000 do 60,000
- Flash point (TCC), °C (°F) >93 (>200)

Adhesive after mixing ingredients:
- Appearance: cream no-transparent paste
- Mixing ratio by volume (resin / hardener): 2:1
- Mixing ratio by weight (resin / hardener): 100:50
- Maximum gap (mm): 3
- Duration of mixed glue in 22°C : 60 min
- Fixing time (light loads, 0,1 N/mm²) w 22°C: 180 min

TYPICAL PROPERTIES OF CURED MATERIAL (samples 1,2 mm thick hardened 7 days in 22 °C) :
  • Dielectric breakdown strength, (ASTM D149) KV/mm : 30
  • Tensile strength ASTM D882, N/mm² : 32
  • Elongation ASTM D882, % : 3
  • Tensile modulus (ASTM D882) N/mm² : 1718
  • Glass transition temperature Tg (ASTM E1640-99) °C : 62
  • Hardness ASTM D1706, Shore D: 60

FUNCTIONAL PROPERTIES OFCURED MATERIAL (cured for 5 days at 22 ° C, unless stated otherwise) :
Shear strength, ASTM D1002/EN 1465 (0,05 mm gap, unless stated otherwise) :
  • Steel, construction steel (shot-blasted) : 37 N/mm²
  • Aluminum, ground with sandpaper (waterproof), grain P400A : 26 N/mm²
  • Aluminum (anodised) : 17,9 N/mm²
  • Galvanized steel : 8,5 N/mm²
  • Stainless steel : 23 N/mm²
  • Polycarbonate : 5,3 N/mm²
  • Nylon : 1,6 N/mm²
  • Wood (fir) : 11,3 N/mm²
  • GRP (polyester resin reinforced with fiberglass) : 5
  • ABS : 4,7

Full technical information can be found in the technical data sheet.