Product description:
LOCTITE 5188 is a form-in-place gasketing product. It is designed for use on rigid metal flanged connections, such as gearboxes and engine casings, particularly where minor oil contamination of the flange surfaces can occur. It cures between close fitting metal surfaces in the absence of air and is particularly suitable for use on aluminum substrates where very good adhesion is achieved. It also provides resistance to low pressures immediately after assembly (instant seal). This product may be dispensed by hand or robotically with the appropriate LOCTITE product conditioning and dispensing systems.Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. Use LOCTITE SF 7063.
2. The product is designed for close fitting flanged parts.
3. LOCTITE automatic dispensing equipment is recommended for best results. Application by screen printing, roller coating or bead dispense can also be achieved manually.
4. To obtain best results, each application should be evaluated under the specific conditions anticipated for dispensing, performance and durability of the parts.
5. Low pressures (<0,05 MPa, psi) may be used when testing to confirm a complete seal immediately after assembly and before curing.
6. Flanges should be tightened as soon as possible after assembly to avoid shimming.

Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: For pack sizes less than 850 mL, the proper storage temperature is 8 °C to 21 °C. For pack sizes of 850 mL or larger, storage should be between 2°C and 8°C. Storage outside these ranges can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assumeresponsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Parameters:
  • Strength : medium
  • Viscosity : high
  • Specific gravity ( 25 °C ) : 1,1
  • Cured for 24 hours at temperature 22 °C:
    Shear strength:
    -Grit Blasted Mild Steel [N/mm²]: ≥2,0
    -Aluminum [N/mm²] :≥3,0
  • Cured for 72 hours at 22 °C:
    Shear strength, ISO 4587:
    -Grit Blasted Mild Steel [N/mm²] : 9,2
    -Aluminum [N/mm²]: 7,0

    Full technical information can be found in the technical data sheet.