Product description:
LOCTITE 435 is a rubber toughened adhesive with increased flexibility and peel strength along with enhancedresistance to shock. The product provides rapid bonding on a wide range of materials, including metals, plastics andelastomers, as well as porous and absorbent materials like wood, paper, leather and fabric.

ISO-10993:
An ISO 10993 Test Protocol is an integral part of the Quality Program for LOCTITE 435. LOCTITE 435 has been qualified to Henkel's ISO 10993 Protocol as a means to assist in the selection of products for use in the medical device industry. Certificates of Compliance are available on Henkel's website or through the Henkel Quality Department. Note: This is a regional approval. Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. Use LOCTITE SF 7063.
2. This product performs best in thin bond gaps (0,05 mm).
3. Excess adhesive can be dissolved with Loctite cleanup solvents, nitromethane or acetone.

Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Parameters:
Curing time (up to a shear strength of 0.1 N / mm²), at 22 ° C and 50% relative humidity:
  • Steel (degreased) : 30 to 45 s
  • Aluminum (purified with isopropanol) : < 60 s
  • Zinc dichromate : 90 to 105 s
  • Neoprene : 30 to 45 s
  • Nitrile rubber : <5 s
  • SBR : 90 to 105 s
  • ABS : 10 to 20 s
  • PVC : 60 to 75 s
  • Polycarbonate : 45 do 60 s
  • Phenolic :10 to 20 s
  • Epoxy G10 : 45 to 60 s
  • Wood (oak) : 75 to 90 s
  • Wood(balsa) : <5 s
Lap Shear Strength, ISO 4587. Cured for 24 hours at 22 °C:
  • Steel (grit blasted), N/mm² : 19
  • Aluminum, N/mm² : 15
  • Nitrile, N/mm² : 0.4
  • EPDM, N/mm² : 0.5
Block Shear Strength, ISO 13445:
  • ABS, N/mm² : 14
  • PVC, N/mm² : 9
  • Polycarbonate, N/mm² : 6
  • Phenolic, N/mm² : 13
  • G-10 Epoxy, N/mm² : 20
Tensile Strength, ISO 6922:
  • Steel (grit blasted), N/mm² : 30
  • Buna-N, N/mm² : 3
Lap Shear Strength, ISO 4587. Cured for 48 hours at 22 °C:
  • Steel (grit blasted), N/mm² : ≥15

Full technical information can be found in the technical data sheet.