LOCTITE Stycast 2762 FT - 1kg
No.
IDH.1189375
LOCTITE Stycast 2762 FT - 1kg
Product description:
LOCTITE STYCAST 2762FT epoxy encapsulant is designed for potting electronic components exposed to harsh environments. Thismaterial is also ideal for large and complex castings that require high temperature resistance and thermal conductivity. LOCTITE STYCAST 2762FT can be used with a variety of catalysts. For more information on mixed properties when used with other available catalysts, please contact your local technical service representative for assistance and recommendations. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
1. Complete cleaning of the components and substrates should be performed to remove contamination such as dust, moisture, saltand oils which can cause electrical failure, poor adhesion or corrosion in an embedded part.
2. Some filler settling is common during shipping and storage. For this reason, it is recommended that the contents of the shipping container be thoroughly mixed prior to use.
3. Power mixing is preferred to ensure a homogeneous product.
4. Accurately weigh resin and hardener into a clean container in the recommended ratio. Weighing apparatus having an accuracy in proportion to the amounts being weighed should be used.
5. Blend components by hand, using a kneading motion, for 2 to 3 minutes and scrape the bottom and sides of the mixing containerfrequently to produce a uniform mixture.
6. If possible, power mix for an additional 2 to 3 minutes. Avoid high mixing speeds. This can entrap excessive amounts of air. It canalso cause overheating of the mixture, resulting in reduced working life.
7. To ensure a void-free embedment, vacuum deairing should be used to remove any entrapped air introduced during the mixing operation.
8. Vacuum deair mixture at 1 to 5 mm mercury. The foam will rise several times the liquid height and then subside.
9. Continue vacuum deairing until most of the bubbling has ceased. This usually takes 3 to 10 minutes.
10. Pour mixture into cavity or mold.
11. To facilitate deairing in difficult to deair materials, add 1 to 3 drops of an air release agent, such as ANTIFOAM 88 into 100 grams of mixture.
12. Gentle warming will also help, but pot life will be shortened.
13. Pour mixture into cavity or mold.
14. Gentle warming of the mold or assembly reduces the viscosity. This improves the flow of the material into the unit having intricate shapes or tightly packed coils or components.
15. Further vacuum deairing in the mold may be required for critical applications.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling. Optimal Storage : 25 °C. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:Hardness, Shore D : 94 Thermal Conductivity, W/(m-K) : 1.34 Operating temperature, ºC : -20 to +230
LOCTITE STYCAST 2762FT with LOCTITE CAT 14 Mixed Density , g/cm³ : 2.31 Mix Ratio, Material:Catalyst, by weight : 100:8 Work Life, 100 grams, at 25ºC, hours : >24
LOCTITE STYCAST 2762FT with LOCTITE CAT 17 Mixed Viscosity, Brookfield , mPa·s (cP) : 150,000 Mixed Density , g/cm³ : 2.23 Mix Ratio, Material:Catalyst, by weight : 100:10 Work Life, 100 grams, at 25ºC, hours : >24
LOCTITE STYCAST 2762FT with LOCTITE CAT 17M-1 Mixed Viscosity, Brookfield , mPa·s (cP) : 150,000 Mixed Density , g/cm³ : 2.23 Mix Ratio, Material:Catalyst, by weight : 100:10 Work Life, 100 grams @ 25ºC, hours : 24
Further information can be found in technical data sheet
LOCTITE STYCAST 2762FT epoxy encapsulant is designed for potting electronic components exposed to harsh environments. Thismaterial is also ideal for large and complex castings that require high temperature resistance and thermal conductivity. LOCTITE STYCAST 2762FT can be used with a variety of catalysts. For more information on mixed properties when used with other available catalysts, please contact your local technical service representative for assistance and recommendations. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
1. Complete cleaning of the components and substrates should be performed to remove contamination such as dust, moisture, saltand oils which can cause electrical failure, poor adhesion or corrosion in an embedded part.
2. Some filler settling is common during shipping and storage. For this reason, it is recommended that the contents of the shipping container be thoroughly mixed prior to use.
3. Power mixing is preferred to ensure a homogeneous product.
4. Accurately weigh resin and hardener into a clean container in the recommended ratio. Weighing apparatus having an accuracy in proportion to the amounts being weighed should be used.
5. Blend components by hand, using a kneading motion, for 2 to 3 minutes and scrape the bottom and sides of the mixing containerfrequently to produce a uniform mixture.
6. If possible, power mix for an additional 2 to 3 minutes. Avoid high mixing speeds. This can entrap excessive amounts of air. It canalso cause overheating of the mixture, resulting in reduced working life.
7. To ensure a void-free embedment, vacuum deairing should be used to remove any entrapped air introduced during the mixing operation.
8. Vacuum deair mixture at 1 to 5 mm mercury. The foam will rise several times the liquid height and then subside.
9. Continue vacuum deairing until most of the bubbling has ceased. This usually takes 3 to 10 minutes.
10. Pour mixture into cavity or mold.
11. To facilitate deairing in difficult to deair materials, add 1 to 3 drops of an air release agent, such as ANTIFOAM 88 into 100 grams of mixture.
12. Gentle warming will also help, but pot life will be shortened.
13. Pour mixture into cavity or mold.
14. Gentle warming of the mold or assembly reduces the viscosity. This improves the flow of the material into the unit having intricate shapes or tightly packed coils or components.
15. Further vacuum deairing in the mold may be required for critical applications.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling. Optimal Storage : 25 °C. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
LOCTITE STYCAST 2762FT with LOCTITE CAT 14
LOCTITE STYCAST 2762FT with LOCTITE CAT 17
LOCTITE STYCAST 2762FT with LOCTITE CAT 17M-1
Further information can be found in technical data sheet