Product description:
LOCTITE 495 is a general purpose cyanoacrylate instant adhesive. The rate of cure will depend on the bondline gap. Thin bond lines result in high cure speeds, increasing the bond gap will decrease the rate of cure. he rate of cure will depend on the ambient relativehumidity. The best results are achieved when the relative humidity in the working environment is 40% to 60% at 22°C. Lower humidity leads to slower cure. Higher humidity accelerates it, but may impair the final strength of the bond. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
1. Bond areas should be clean and free from grease. Clean all surfaces with a LOCTITE SF 7063 cleaning solvent and allow to dry.
2. To improve bonding on low energy plastic surfaces, LOCTITE 770 Primer may be applied to the bond area. Avoid applying excess Primer. Allow the Primer to dry.
3.Activator LOCTITE SF 7455 may be used if necessary. Apply it to one bond surface (do not apply activator to the primed surface where Primer is also used). Allow the Activator to dry.
4. Apply adhesive to one of the bond surfaces (do not apply the adhesive to the activated surface). Do not use items like tissue or a brush to spread the adhesive. Assemble the parts within a few seconds. The parts should be accurately located, as the short fixture time leaves little opportunity for adjustment.
5. Activator LOCTITE SF 7455 can be used to cure fillets of product outside the bond area. Spray or drop the activator on the excess product.
6. Bonds should be held fixed or clamped until adhesive has fixtured.
7. Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling. Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
Curing speed depending on the material (temperature 22 ° C, humidity 50%):
Shear strength depending on material after 24 hours (temperature 22 ° C):
Tensile strength :
Full technical information can be found in the technical data sheet.
LOCTITE 495 is a general purpose cyanoacrylate instant adhesive. The rate of cure will depend on the bondline gap. Thin bond lines result in high cure speeds, increasing the bond gap will decrease the rate of cure. he rate of cure will depend on the ambient relativehumidity. The best results are achieved when the relative humidity in the working environment is 40% to 60% at 22°C. Lower humidity leads to slower cure. Higher humidity accelerates it, but may impair the final strength of the bond. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
1. Bond areas should be clean and free from grease. Clean all surfaces with a LOCTITE SF 7063 cleaning solvent and allow to dry.
2. To improve bonding on low energy plastic surfaces, LOCTITE 770 Primer may be applied to the bond area. Avoid applying excess Primer. Allow the Primer to dry.
3.Activator LOCTITE SF 7455 may be used if necessary. Apply it to one bond surface (do not apply activator to the primed surface where Primer is also used). Allow the Activator to dry.
4. Apply adhesive to one of the bond surfaces (do not apply the adhesive to the activated surface). Do not use items like tissue or a brush to spread the adhesive. Assemble the parts within a few seconds. The parts should be accurately located, as the short fixture time leaves little opportunity for adjustment.
5. Activator LOCTITE SF 7455 can be used to cure fillets of product outside the bond area. Spray or drop the activator on the excess product.
6. Bonds should be held fixed or clamped until adhesive has fixtured.
7. Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling. Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
Curing speed depending on the material (temperature 22 ° C, humidity 50%):
- Steel (degreased) : 10 to 30 s
- Aluminum (degreased) : 5 to 15 s
- Zinc dichromate : 30 to 90 s
- Nitrile rubber : < 5 s
- ABS : 10 to 30 s
- Neoprene : < 5 s
- PCV : 3 to 10 s
- Polycarbonate : 20 to 60 s
- Phenolic : 5 to 20 s
Shear strength depending on material after 24 hours (temperature 22 ° C):
- Shot-blasted steel : 12 to 26 N/mm²
- Aluminum (etched) : 12 to 19 N/mm²
- Zinc dichromate : 6 to 13 N/mm²
- ABS : 6 to 20 N/mm²
- PCV : 6 to 20 N/mm²
- Polycarbonate : 5 to 20 N/mm²
- Phenolic : 5 to 15 N/mm²
- Neoprene : 5 to 15 N/mm²
- Nitrile rubber : 5 to 15 N/mm²
Tensile strength :
- Shot-blasted steel : 12 to 25 N/mm²
- Buna N rubber : 5 to 15 N/mm²
Full technical information can be found in the technical data sheet.