TEROSON WT 112 DB - 40kg (soundproofing spray mass)

TEROSON WT 112 DB - 40kg (soundproofing spray mass) (IDH.691488)

Product description:
TEROSON WT 112 DB is a secondary noise and vibration control mass for spray and spatula application, based on an aqueous synthetic resin dispersion with flame retardant additives. The product is rendered environmentally friendly by the use of low toxicity raw materials (halogen, heavy metal and asbestos free). TEROSON WT 112 DB fulfils fire protection requirements in rail with classification HL 3 according to DIN EN 45545-2 (2016-02) and marine with MED 3/18.a – Module B +D certificate based on IMO resolution MSC.307(88) FTPC2010, annex 1, part 5. In addition to high acoustic effectiveness the product also demonstrates thermal insulation properties. TEROSON WT 112 DB demonstrates reliable adhesion to stainless steel, galvanized steel sheets and anodized aluminium. Non galvanized sheet steel and raw aluminium surfaces will firstly require application with effective corrosion protection (primer coated or painted). The sag resistance on vertical surfaces, when spray applied, is a minimum of 6 mm, based on one application layer. TEROSON WT 112 DB can also be applied by hand, e.g. spatula. However, we only recommend this application method for smaller areas or touch-up jobs. During the drying process, no cracks occur in large, flat coated surfaces. If material is allowed to pile up in grooves or at corners, and if unfavourable drying conditions ensue, e.g. absence of convection, this may give rise to occasional hairline fractures. Further information about the product: biuro@woronko-kleje.pl

Directions for use:
The surfaces to be coated must be dry, free of oil, dust, grease and other contaminants. An adhesion promoter is not necessary. Non-galvanized steel sheet and non-anodized aluminium, however, require coating with a suitable water retardant corrosion protection.If necessary, TEROSON WT 112 DB must be stirred before use when it has been stored between delivery and use for longer period (approx. 3 months). TEROSON WT 112 DB is supplied in ready to use condition for application by secondary air spraying using piston pumps. Following values are recommended for spraying:
-Conveyance, with a piston pump, ratio : 12 : 1
-Material pressure, bar : 2 to 4
-Atomizing air pressure, bar : 4 to 6
-Nozzle, mm Ø : 6

Applications with other spray technologies, e.g. airless pumps is, in principle, also possible. Trials are however, recommended. The material can be spray applied - even overhead and on vertical surfaces - up to a wet film layer thickness of 6 mm in one step. Application temperature range possible is 10°C to 40°C; optimum temperature is 15°C to 25°C. Dilution with water (max. 5%) is possible, but should only be conducted in exceptional cases. Possible disadvantages: reduced sag resistance on vertical surfaces, delayed drying, crack formation. Therefore dilution is only recommended for small surfaces and repair work.

Storage:
  • Recommended storage temperature, °C : 15 to 25
  • Shelf-life (in unopened original packaging) : 9 months
  • Frost-Sensitive : yes

    Parameters:
  • Color: light gray to light beige
  • Odor: weak alcohol
  • Consistency: thick suspension
  • Density:
    - wet: approx. 1,4 g/cm3
    - dry: approx. 1,2 g/cm3
  • Solids content: approx. 65%
  • pH value: approx. 9
  • Consumption per 1 mm of dry layer: approx. : 1,4 kg/m2
  • Thermal conductivity (DIN 52612) approx. : 0,21 W/mK
  • Application temperature: 10 °C to 40 °C
  • Application temperature: - 50 °C to 120 °C (short time up to 1 hour): 160 °C

    Full technical information can be found in the technical data sheet.