Product description:
LOCTITE 6300 is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absenceof air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include holding gears and sprockets onto gearbox shafts and rotors on electric motor shafts. LOCTITE 6300 is part of the Health and Safety anaerobic range. The product is label free. There are no risk or safety phrases associated with either the formulation or its ingredients. Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
FOR ASSEMBLY:
1. For best results, clean all surfaces (external and internal) with a LOCTITE SF 7063 cleaning solvent and allow to dry.
2. If the material is an inactive metal or the cure speed is too slow, spray with activator LOCTITE SF 7471 or LOCTITE SF 7649 and allow to dry.
3. For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.
4. For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.
5. For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.
6. Parts should not be disturbed until sufficient handling strength is achieved.

FOR DISASSEMBLY:
7. Apply localized heat to the assembly to approximately 250 °C. Disassemble while hot.

FOR CLEAN UP:
8. Cured product can be removed with a combination of soaking in a LOCTITE SF 7200 solvent and mechanical abrasion such as a wire brush.

Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Parameters:
  • Shear strength after 24 hours (gap =0,15 mm) : 10 N/mm²
  • Time to get full strength (22 °C):
    -Steel : 72 hours.
    -Stainless steel : 80 hours
    -Aluminum : 80 hours
  • Time to obtain initial strength (22 °C):
    -Steel : 10 minutes
    -Stainless steel: 2 hours
    -Aluminum : 10 minutes
  • Working temperature : from -55 °C to +180 °C
  • Color : green


Full technical information can be found in the technical data sheet.