TEROSON PU 6700 - 50ml (polyurethane adhesive) /Teromix 6700
No.
IDH.264880
Associated products:
- TEROSON ET QUAD ST MIX SMALL (for 50 ml cartridges 1:1, 1:2) (IDH.2900614)
- LOCTITE 96001 (manual applicator for 50ml cartridges, mixing ratio of components A&B 1:1 or 1:2) (IDH.267452)
- LOCTITE 97956 (adapter for double (1:1) 50ml cartridges, compatible with standard 300ml cartridge squeezers) (IDH.476895A)
TEROSON PU 6700 - 50ml (polyurethane adhesive) /Teromix 6700
Associated products:
- TEROSON ET QUAD ST MIX SMALL (for 50 ml cartridges 1:1, 1:2) (IDH.2900614)
- LOCTITE 96001 (manual applicator for 50ml cartridges, mixing ratio of components A&B 1:1 or 1:2) (IDH.267452)
- LOCTITE 97956 (adapter for double (1:1) 50ml cartridges, compatible with standard 300ml cartridge squeezers) (IDH.476895A)
Product description:
TEROSON PU 6700 is a polyurethane based two-component adhesive which cures at room temperature. For accelerated curing it is recommended to increase the temperature up to 60 to 70 °C. TEROSON PU 6700 can be painted with standard commercial car repair refinishing paints. Application Areas: TEROSON PU 6700 is used in the automotive industry and in motor vehicle body repair shops mainly for bonding plastic parts (e.g. customising body parts) as well as metal parts. For bonding plastic parts we recommend the use of TEROSON 150. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Pretreatment:
The parts to be bonded must be free from oil, grease, moisture, dirt and release agents. Metals may either be primed (e.g. cathodic EC) or they should be grinded. Finally the parts should be cleaned with TEROSON VR 20.
Application:
Insert the cartridge into a suitable application gun. Apply pressure to the cartridge(s) to ensure a simultaneous and homogeneous flow of both components. Thereafter, attach the static mixer and cut the tip to provide for the desired bead size. Discard the first 2 cm of extruded adhesive bead. TEROSON PU 6700 is applied directly to the substrates. Any excess material should be removed immediately after application. If material is left in the cartridge leave the static mixer attached. For further use of the product, simply remove the mixer and install a new one. (As described above).
Curing:
Curing occurs at room temperature. To get a faster grindability the parts bonded with TEROSON PU 6700 can bewarmed up to 60 to 70 °C for minimum 15 minutes.
Cleaning:
Freshly applied and uncured material should be removed with a dry cloth and then cleaned off with a suitable solvent. Cured adhesive can only be removed mechanically.
Storage:
Frost sensitive : no Recommended storage temperature :10 to 25 °C Shelf life : 12 months in original packaging
Parameters:
COMPONENT A:
Full technical information can be found in the techncial data sheet.
TEROSON PU 6700 is a polyurethane based two-component adhesive which cures at room temperature. For accelerated curing it is recommended to increase the temperature up to 60 to 70 °C. TEROSON PU 6700 can be painted with standard commercial car repair refinishing paints. Application Areas: TEROSON PU 6700 is used in the automotive industry and in motor vehicle body repair shops mainly for bonding plastic parts (e.g. customising body parts) as well as metal parts. For bonding plastic parts we recommend the use of TEROSON 150. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Pretreatment:
The parts to be bonded must be free from oil, grease, moisture, dirt and release agents. Metals may either be primed (e.g. cathodic EC) or they should be grinded. Finally the parts should be cleaned with TEROSON VR 20.
Application:
Insert the cartridge into a suitable application gun. Apply pressure to the cartridge(s) to ensure a simultaneous and homogeneous flow of both components. Thereafter, attach the static mixer and cut the tip to provide for the desired bead size. Discard the first 2 cm of extruded adhesive bead. TEROSON PU 6700 is applied directly to the substrates. Any excess material should be removed immediately after application. If material is left in the cartridge leave the static mixer attached. For further use of the product, simply remove the mixer and install a new one. (As described above).
Curing:
Curing occurs at room temperature. To get a faster grindability the parts bonded with TEROSON PU 6700 can bewarmed up to 60 to 70 °C for minimum 15 minutes.
Cleaning:
Freshly applied and uncured material should be removed with a dry cloth and then cleaned off with a suitable solvent. Cured adhesive can only be removed mechanically.
Storage:
Parameters:
COMPONENT A:
- Color: beige
- Density: 1,4 g/cm³
- Color: black
- Density approx. : 1,7 g/cm³
- Color : dark grey
- Curing time at 23 °C approx. : 6 hr(s)
- Hardness, Shore'a A : approx. : 90
- Shear strength:
-After 2 days( temperature 23 °C, 50 % rh) : approx. 13 MPa
Full technical information can be found in the techncial data sheet.