LOCTITE SI 5610 - 400ml (Silicone adhesive)
No.
IDH.2056417
Associated products:
- Mixing nozzle Stat Mixer MC08-24 (1:1 and 2:1), Type No. 98457, for 400 ml catridges (IDH.720174A)
- LOCTITE Universal Fixmaster Dispenser 200ml, 400ml, 490ml, manual gun (IDH.1372751)
- LOCTITE EQ HD 14 400ml 2K (pneumatic dispenser for 2K cartridges) (IDH.2693825)
- LOCTITE EQ HD 14 400ml 2K (manual dispenser for 2K cartridges) (IDH.2693823)
LOCTITE SI 5610 - 400ml (Silicone adhesive)
Associated products:
- Mixing nozzle Stat Mixer MC08-24 (1:1 and 2:1), Type No. 98457, for 400 ml catridges (IDH.720174A)
- LOCTITE Universal Fixmaster Dispenser 200ml, 400ml, 490ml, manual gun (IDH.1372751)
- LOCTITE EQ HD 14 400ml 2K (pneumatic dispenser for 2K cartridges) (IDH.2693825)
- LOCTITE EQ HD 14 400ml 2K (manual dispenser for 2K cartridges) (IDH.2693823)
Product description:
LOCTITE 5610 is a two part, fast cure silicone with excellent bond strength to glass, metals and Ceran. LOCTITE 5610 has excellent hot strength up to 180 °C with the capability to resist higher temperatures for short-term exposure. Typical applications include sealing/bonding glass stovetop assemblies, weld and rivet reduction in high temperature applications, and other high temperature bondingapplications. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
1. For best performance the mating surface should be clean and free of grease. Use LOCTITE SF 7063.
2. Best results are achieved utilizing a helix 8mm diameter, 24 element mix nozzle.
3. After dispense, mate parts immediately to ensure maximum bond strength.
4. Dual Cartridges: Insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Next, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. Attach the static mixing nozzle to the end of the cartridge and begin dispensing the adhesive. Purge and dispose of the first 3 - 5 cm from the end of the mix nozzle, as it may not be sufficiently mixed. Bulk Containers: Utilize volumetric dispense system to ensure proper mix ratio and utilize mix nozzle to obtain adequate mixing.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
TYPICAL PARAMETERS OF CURED MATERIAL
Shear strength, ISO 4587 (Cured for 7 days in 22 °C):Aluminum (Alclad), N/mm² : 2,3 Carbon steel (after abrasive blasting), N/mm² : 1,8 Stainless steel, N/mm² : 2,3 ABS, N/mm² : 2,3 PVC, N/mm² : 2,3 Polycarbonate, N/mm² : 2,3 Glass fiber reinforced epoxide, N/mm² : 2,1 Nylon 66, N/mm² : 0,8 Wood (teak), N/mm² : 1,7
Full technical information can be found in the technical data sheet.
LOCTITE 5610 is a two part, fast cure silicone with excellent bond strength to glass, metals and Ceran. LOCTITE 5610 has excellent hot strength up to 180 °C with the capability to resist higher temperatures for short-term exposure. Typical applications include sealing/bonding glass stovetop assemblies, weld and rivet reduction in high temperature applications, and other high temperature bondingapplications. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
1. For best performance the mating surface should be clean and free of grease. Use LOCTITE SF 7063.
2. Best results are achieved utilizing a helix 8mm diameter, 24 element mix nozzle.
3. After dispense, mate parts immediately to ensure maximum bond strength.
4. Dual Cartridges: Insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Next, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. Attach the static mixing nozzle to the end of the cartridge and begin dispensing the adhesive. Purge and dispose of the first 3 - 5 cm from the end of the mix nozzle, as it may not be sufficiently mixed. Bulk Containers: Utilize volumetric dispense system to ensure proper mix ratio and utilize mix nozzle to obtain adequate mixing.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
TYPICAL PARAMETERS OF CURED MATERIAL
Shear strength, ISO 4587 (Cured for 7 days in 22 °C):
Full technical information can be found in the technical data sheet.