TEROSON PU 9225 SF - 50ml (polyurethane adhesive for plastics, fast)/Terokal 9225
No.
IDH.882088
Associated products:
- TEROSON 150 - 150ml (plastic primer) / Terokal 150 (IDH.267078)
- TEROSON PU 9225 - 250ml (polyurethane adhesive)/Terokal 9225 (IDH.881837)
- TEROSON PU 9225 UF ME - 50ml (polyurethane adhesive for plastics, ultrafast) (IDH.1786434)
- TEROSON VR 10 - 1l (cleaner) / Reiniger FL (IDH.2558379)
- TEROSON ET QUAD ST MIX SMALL (for 50 ml cartridges 1:1, 1:2) (IDH.2900614)
- TEROSON PU 9225 - 50ml (klej poliuretanowy)/Terokal 9225 (IDH.267081)
- LOCTITE 97956 (adapter for double (1:1) 50ml cartridges, compatible with standard 300ml cartridge squeezers) (IDH.476895A)
- LOCTITE 96001 (manual applicator for 50ml cartridges, mixing ratio of components A&B 1:1 or 1:2) (IDH.267452)
Files to download:
Multimedia:
TEROSON PU 9225 SF - 50ml (polyurethane adhesive for plastics, fast)/Terokal 9225
Associated products:
- TEROSON 150 - 150ml (plastic primer) / Terokal 150 (IDH.267078)
- TEROSON PU 9225 - 250ml (polyurethane adhesive)/Terokal 9225 (IDH.881837)
- TEROSON PU 9225 UF ME - 50ml (polyurethane adhesive for plastics, ultrafast) (IDH.1786434)
- TEROSON VR 10 - 1l (cleaner) / Reiniger FL (IDH.2558379)
- TEROSON ET QUAD ST MIX SMALL (for 50 ml cartridges 1:1, 1:2) (IDH.2900614)
- TEROSON PU 9225 - 50ml (klej poliuretanowy)/Terokal 9225 (IDH.267081)
- LOCTITE 97956 (adapter for double (1:1) 50ml cartridges, compatible with standard 300ml cartridge squeezers) (IDH.476895A)
- LOCTITE 96001 (manual applicator for 50ml cartridges, mixing ratio of components A&B 1:1 or 1:2) (IDH.267452)
Product description:
TEROSON PU 9225 SF is a polyurethane based two-component adhesive which cures at room temperature. For accelerated curing it is recommended to increase the temperature up to 60 to 70 °C. The product is supplied in a convenient twin cartridge and is rapid-curing. TEROSON PU 9225 SF can be painted with standard commercial car repair refinishing paints. When applying TEROSON PU 9225 SF to plastics the use of an approved Henkel primer is absolutely necessary. Detailed information see directions of use. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Pretreatment:
The parts to be bonded must be free from oil, grease, moisture, dirt and release agents. Pre-cleaning with a high pressure injection cleaner is recommended. After drying the parts should be cleaned and pretreated with TEROSON VR 20. Damaged plastic parts have to be sanded on the face side with a narrow belt sander (grit P 80 to 120) to grind a V-groove (1 to 2 cm). Finally the sanded parts should be cleaned and pretreated with TEROSON VR 20. When applying TEROSON PU 9225 SF to plastics the use of primer TEROSON 150 in a thin layer is necessary. Evaporation time is approx. 10 minutes.
Application:
Insert the cartridge into a suitable application gun. Apply pressure to the cartridge(s) to ensure a simultaneous and homogeneous flow of both components. Thereafter, attach the static mixer and cut the tip to provide for the desired bead size. Discard the first 2 cm of extruded adhesive bead. TEROSON PU 9225 SF is applied directly to the substrates. Any excess material should be removed immediately after application. If material is left in the cartridge leave the static mixer attached. For further use of the product, simply remove the mixer and install a new one. In case of plastic repair the use of woven fibreglass mat is recommended for reinforcing.
Reinforcing:
In the case of simple cracks TEROSON PU 9225 SF can be applied in one step to both, the face side and the rear side. For more difficult damages, the adhesive should be applied to both sides separately. Start with two continuous beads on the rear side and place them to both sides of the damaged area (bond with minimum 100 mm). For large damages e.g. holes, it is recommended to reinforce the complete damaged area with woven fibre glass mat by incorporating the mat in the beads. Reinforce initial crack areas with woven glass fibre mat in the same way. Then apply TEROSON PU 9225 SF on top of the reinforced matting and smooth the surface. Ensurethat the adhesive is pressed through the crack and the fibre glass mat to the front side to guarantee a reliable bonding.During applying TEROSON PU 9225 SF, keep the mixer tip within the material to avoid air inclusions. Apply an excess ofTEROSON PU 9225 SF in the same way to the front side.
Curing:
Curing occurs at room temperature. For accelerated curing it is recommended to use a heat source. To get a fastergrindability the parts bonded with TEROSON PU 9225 SF can be warmed up to 60 to 70 °C for minimum 3 to 4 minutes.
Storage:
Frost sensitive : no Recommended storage temperature : 10 to 25 °C Shelf life : 12 months
Parameters:
COMPONENT A:
Full technical information can be found in the techncial data sheet.
TEROSON PU 9225 SF is a polyurethane based two-component adhesive which cures at room temperature. For accelerated curing it is recommended to increase the temperature up to 60 to 70 °C. The product is supplied in a convenient twin cartridge and is rapid-curing. TEROSON PU 9225 SF can be painted with standard commercial car repair refinishing paints. When applying TEROSON PU 9225 SF to plastics the use of an approved Henkel primer is absolutely necessary. Detailed information see directions of use. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Pretreatment:
The parts to be bonded must be free from oil, grease, moisture, dirt and release agents. Pre-cleaning with a high pressure injection cleaner is recommended. After drying the parts should be cleaned and pretreated with TEROSON VR 20. Damaged plastic parts have to be sanded on the face side with a narrow belt sander (grit P 80 to 120) to grind a V-groove (1 to 2 cm). Finally the sanded parts should be cleaned and pretreated with TEROSON VR 20. When applying TEROSON PU 9225 SF to plastics the use of primer TEROSON 150 in a thin layer is necessary. Evaporation time is approx. 10 minutes.
Application:
Insert the cartridge into a suitable application gun. Apply pressure to the cartridge(s) to ensure a simultaneous and homogeneous flow of both components. Thereafter, attach the static mixer and cut the tip to provide for the desired bead size. Discard the first 2 cm of extruded adhesive bead. TEROSON PU 9225 SF is applied directly to the substrates. Any excess material should be removed immediately after application. If material is left in the cartridge leave the static mixer attached. For further use of the product, simply remove the mixer and install a new one. In case of plastic repair the use of woven fibreglass mat is recommended for reinforcing.
Reinforcing:
In the case of simple cracks TEROSON PU 9225 SF can be applied in one step to both, the face side and the rear side. For more difficult damages, the adhesive should be applied to both sides separately. Start with two continuous beads on the rear side and place them to both sides of the damaged area (bond with minimum 100 mm). For large damages e.g. holes, it is recommended to reinforce the complete damaged area with woven fibre glass mat by incorporating the mat in the beads. Reinforce initial crack areas with woven glass fibre mat in the same way. Then apply TEROSON PU 9225 SF on top of the reinforced matting and smooth the surface. Ensurethat the adhesive is pressed through the crack and the fibre glass mat to the front side to guarantee a reliable bonding.During applying TEROSON PU 9225 SF, keep the mixer tip within the material to avoid air inclusions. Apply an excess ofTEROSON PU 9225 SF in the same way to the front side.
Curing:
Curing occurs at room temperature. For accelerated curing it is recommended to use a heat source. To get a fastergrindability the parts bonded with TEROSON PU 9225 SF can be warmed up to 60 to 70 °C for minimum 3 to 4 minutes.
Storage:
Parameters:
COMPONENT A:
- Color: yelow
- Density: 1,4 g/cm³
- Color: black
- Density approx. : 1,7 g/cm³
- Color : dark grey
- Curing time at 23 °C approx. : 1.5 hr(s)
- Layer thickness: 3 mm - Hardness, Shore'a A : approx. : 90
- Shear strength:
-After 2 days( temperature 23 °C, 50 % rh) : approx. 13 MPa
Full technical information can be found in the techncial data sheet.