BONDERITE M-NT 1455-W CONVERSION COATING (soaked wipes forming a conversion coating, 50 pcs)
No.
IDH.2156526
Product description:
BONDERITE M-NT 1455-W is a chromium free and waterbased corrosion protecting surface treatment for metals like aluminum, zinc, zinc alloy, cold- and hot rolled steel, stainless steel, galvanized, sand basted and armor plate surfaces. The corrosion protection in BONDERITE M-NT 1455-W seperates the surface of the above mentioned types of metals. The converted surface provides an excellent base for organic finishes, paint, sealers and most adhesives. This reaction greatly enhances adhesion and corrosion resistance of subsequently applied paints (including primer when multiple coat systems are used), sealers and adhesives. BONDERITE M-NT 1455-W conversion coating process is a dry-in-place application and does not require subsequent cleaning. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Application:
Treating metal surfaces with BONDERITE M-NT 1455-W is the last step before starting with sealing, bonding or paint process. The complete process sequence consists of the following steps:
1. All bare metal surfaces to be converted with BONDERITE M-NT 1455-W must be dry and free from grease, oil and other foreign matter before pre-treatment. Abrasive cleaning is acceptable method of surface preparation where scale or corrosion particles exist. Afterward thoroughly clean and prepare the metal surface using TEROSON VR 10 / VR 20. Follow the application instructions as recommended by Henkel. This is due to Conversion coating can be influenced in a negative manner.
2. Wipe the clean and dry surface with BONDERITE M-NT 1455-W. Use slightly over lapping vertical and horizontal, even with slightly application pressure. Make sure the entire bare metal surface is wetted with fluid. The surface should remain wet for minimum one minute under wiping movements for the chemical reaction. If handling of the dried, treated work is necessary, operators should wear clean, lint free paint gloves so that the treated surface is not contaminated. If the treated surface becomes damaged or re contaminated, go back to the first step above. Drying time should be at least five minutes. Latest after 15 minutes, the following coating process should be done. To use only on bare metal surfaces. Do not use on paint, paint primers, 1K, 2K, residual paint coatings and plastic parts. Not to be used under and on Polyesterfillers.
3. Allow the wetted surface to dry at ambient temperature.
4. Within 15 minutes apply paint, sealer or adhesive over the dry and converted surface. It is necessary to complete the painting, sealing or adhesive bonding operation. Make sure that all treated surface is covered.
Storage:
Recommended Storage Temperature, °C : 10 to 25 Shelf-life, months (in unopened original packaging) : 24 Frost-Sensitive : yes
Parameters:
Concentration : ready to use wipes Application : wet the surface by wipe on Evaporation time : min. 1 minute Open time : max. 15 minutes pH-value : 2.6 Application temperature : 20 to 40 °C
Full technical information can be found in the technical data sheet.
BONDERITE M-NT 1455-W is a chromium free and waterbased corrosion protecting surface treatment for metals like aluminum, zinc, zinc alloy, cold- and hot rolled steel, stainless steel, galvanized, sand basted and armor plate surfaces. The corrosion protection in BONDERITE M-NT 1455-W seperates the surface of the above mentioned types of metals. The converted surface provides an excellent base for organic finishes, paint, sealers and most adhesives. This reaction greatly enhances adhesion and corrosion resistance of subsequently applied paints (including primer when multiple coat systems are used), sealers and adhesives. BONDERITE M-NT 1455-W conversion coating process is a dry-in-place application and does not require subsequent cleaning. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Application:
Treating metal surfaces with BONDERITE M-NT 1455-W is the last step before starting with sealing, bonding or paint process. The complete process sequence consists of the following steps:
1. All bare metal surfaces to be converted with BONDERITE M-NT 1455-W must be dry and free from grease, oil and other foreign matter before pre-treatment. Abrasive cleaning is acceptable method of surface preparation where scale or corrosion particles exist. Afterward thoroughly clean and prepare the metal surface using TEROSON VR 10 / VR 20. Follow the application instructions as recommended by Henkel. This is due to Conversion coating can be influenced in a negative manner.
2. Wipe the clean and dry surface with BONDERITE M-NT 1455-W. Use slightly over lapping vertical and horizontal, even with slightly application pressure. Make sure the entire bare metal surface is wetted with fluid. The surface should remain wet for minimum one minute under wiping movements for the chemical reaction. If handling of the dried, treated work is necessary, operators should wear clean, lint free paint gloves so that the treated surface is not contaminated. If the treated surface becomes damaged or re contaminated, go back to the first step above. Drying time should be at least five minutes. Latest after 15 minutes, the following coating process should be done. To use only on bare metal surfaces. Do not use on paint, paint primers, 1K, 2K, residual paint coatings and plastic parts. Not to be used under and on Polyesterfillers.
3. Allow the wetted surface to dry at ambient temperature.
4. Within 15 minutes apply paint, sealer or adhesive over the dry and converted surface. It is necessary to complete the painting, sealing or adhesive bonding operation. Make sure that all treated surface is covered.
Storage:
Parameters:
Full technical information can be found in the technical data sheet.