TEROSON VR 2200 - 100ml (valve lapping paste)
No.
IDH.142228
TEROSON VR 2200 - 100ml (valve lapping paste)
Product description:
TEROSON VR 2200 coarse and fine, are grinding pastes based on water soluble synthetic oil and corundum abrasives. Both components come together in one can with two separate chambers and openings. The coarse paste is used for pre-grinding and the fine paste is used to achieve the desired surface finish. Both TEROSON VR 2200 compounds are easy to use, do not run off the surfaces to be ground and can, as they are water-soluble, be easily rinsed off the components after grinding. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Application
Before application stir both compounds, fine and coarse, to achieve a homogenous paste. If required, water may be added to thin down the compound.
Practice
For the first step use the coarse paste for grinding the parts to achieve nearly the desired valve seat. The second step requires the fine paste to achieve the desired surface finish and the exact valve seat. After the grinding operation, rinse parts with plenty of water to remove all residual grinding compound and dry parts by using pressurised air.
Storage:Frost sensitive : no Recommended storage temperature : 10 to 25 °C Shelf life : 12 months
Parameters:
Coarse Colour : grey Odour : slight Consistency : viscous liquid Density : approx. 1.95 g/cm³ Abrasive size : 90 to 200 µm
Fine Colour grey Odour : slight Consistency: viscous liquid Density : approx. 1.95 g/cm³ Abrasive size : <90 µm
Further information can be found in technical data sheet
TEROSON VR 2200 coarse and fine, are grinding pastes based on water soluble synthetic oil and corundum abrasives. Both components come together in one can with two separate chambers and openings. The coarse paste is used for pre-grinding and the fine paste is used to achieve the desired surface finish. Both TEROSON VR 2200 compounds are easy to use, do not run off the surfaces to be ground and can, as they are water-soluble, be easily rinsed off the components after grinding. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Application
Before application stir both compounds, fine and coarse, to achieve a homogenous paste. If required, water may be added to thin down the compound.
Practice
For the first step use the coarse paste for grinding the parts to achieve nearly the desired valve seat. The second step requires the fine paste to achieve the desired surface finish and the exact valve seat. After the grinding operation, rinse parts with plenty of water to remove all residual grinding compound and dry parts by using pressurised air.
Storage:
Parameters:
Coarse
Fine
Further information can be found in technical data sheet