Product description:
LOCTITE STYCAST W 67 encapsulant is designed for high throughput assembly operations. The material's low viscosity andexcellent wetting properties allow for complete impregnation when used either on small slightly wound coils or large castings. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
1. Complete cleaning of the substrates should be performed to remove contamination such as oxide layers, dust, moisture, salt and oils which can cause poor adhesion or corrosion in a bonded part.
2. Accurately weigh resin and hardener into a clean container in the recommended ratio. Weighing apparatus having an accuracy inproportion to the amounts being weighed should be used.
3. Blend components by hand, using a kneading motion, for 2 to 3 minutes and scrape the bottom and sides of the mixing container frequently to produ:ce a uniform mixture.
4. If possible, power mix for an additional 2 to 3 minutes. Avoid high mixing speeds. This can entrap excessive amounts of air. It canalso cause overheating of the mixture, resulting in reducedworking life.
5. To eliminate moisture absorbed in coils, paper, and other insulation components, the part to be impregnated or potted should be preheated to 100 to 120°C.
6. For coil molding, preheat the components and mold to 70 to 90°C prior to pouring.
7. Submerge components in reservoir containing impregnating resin and allow to stand until assembly is completely penetrated by resin mixture.
8. Vacuum can be applied to ensure complete penetration in components containing tightly wound coils.
9. Remove impregnated assembly from reservoir and allow to drain.
Storage:
Store in original, tightly covered containers in clean, dry areas. Storage information may be indicated on the product container labeling.Optimal Storage: 25°C. Storage below 25°C or greater than 25°C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
Viscosity, Brookfield , 25 °C, mPa·s (cP) : 250 Density, g/cm³ : 1.23 Work Life (100 g mass) at 25 °C, days : 30 Shelf Life at 25°C, days : 180 Flexural Strength N/mm² : 116 Compressive Strength, N/mm² : 150 Tensile Strength, N/mm² : 71
Full technical information can be found in the technical data sheet
LOCTITE STYCAST W 67 encapsulant is designed for high throughput assembly operations. The material's low viscosity andexcellent wetting properties allow for complete impregnation when used either on small slightly wound coils or large castings. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
1. Complete cleaning of the substrates should be performed to remove contamination such as oxide layers, dust, moisture, salt and oils which can cause poor adhesion or corrosion in a bonded part.
2. Accurately weigh resin and hardener into a clean container in the recommended ratio. Weighing apparatus having an accuracy inproportion to the amounts being weighed should be used.
3. Blend components by hand, using a kneading motion, for 2 to 3 minutes and scrape the bottom and sides of the mixing container frequently to produ:ce a uniform mixture.
4. If possible, power mix for an additional 2 to 3 minutes. Avoid high mixing speeds. This can entrap excessive amounts of air. It canalso cause overheating of the mixture, resulting in reducedworking life.
5. To eliminate moisture absorbed in coils, paper, and other insulation components, the part to be impregnated or potted should be preheated to 100 to 120°C.
6. For coil molding, preheat the components and mold to 70 to 90°C prior to pouring.
7. Submerge components in reservoir containing impregnating resin and allow to stand until assembly is completely penetrated by resin mixture.
8. Vacuum can be applied to ensure complete penetration in components containing tightly wound coils.
9. Remove impregnated assembly from reservoir and allow to drain.
Storage:
Store in original, tightly covered containers in clean, dry areas. Storage information may be indicated on the product container labeling.Optimal Storage: 25°C. Storage below 25°C or greater than 25°C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
Full technical information can be found in the technical data sheet