Product description:
LOCTITE® PC 7352 is a 100% solid, room temperature curing, two component Polyurea compound. When cured it is a tough and resilient adhesive. This product offers an excellent balance of thixotropic behavior and fast cure. Its fast cure is specially designed for on-site repairs. Typical applications include repair and rebuild conveyor belts and liners in mills, pumps, feeder bowls, hoppers, and chutes. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Surface Preparation
Proper surface preparation is critical to the long-term performance of this product. The exact requirements vary with the severity of the application, expected service life, and initial substrate conditions:

1. Cut away loose and damaged pieces of the rubber to be repaired.
2. Remove dirt, oil, grease, etc. from rubber with a suitable cleaner, e.g. TEROSON® VR 40 or TERSON® VR 10.
3. Abrade the repair area with an abrasive wheel or wire wheel to roughen the bond surface. Avoid overheating and melting the rubber during grinding.
4. Aggressively clean the prepared surfaces with LOCTITE® solvent based cleaner (i.e. TEROSON® VR 40 or TERSON® VR 10) and allow to dry.
5. Apply LOCTITE® Etching agent on clean rubber surface with a brush.
6. Let it act for 30 minutes at 25°C or 60 minutes at 10°C.
Application
1. Insert the cartridge into the application gun and push the plunger into the cylinders using light pressure on the trigger. Then, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. Cut a piece of the staticmixing nozzle to facilitate product flow. Attach the static mixing nozzle to the end of the cartridge.
2. Purge and dispose of the first 3 to 5 cm from the end of the mix nozzle, as it may not be sufficiently mixed. Work quickly as material will begin to cure in static mixer.
3. Work the adhesive onto the substrate with a spatula to allow maximum surface contact and adhesion.
4. It is not necessary to use all the adhesive in the cartridge in one application. Leave the static mixer on the cartridge when application is complete. The mixer serves as a seal and should be discarded and replaced with a fresh mixer for the next application.
Color
1. Color variation is possible between the batches and will not affect the performance of the product.
Clean-up
1. Immediately after use clean tools with a Loctite® solvent base cleaner. Once cured, the material canonly be removed mechanically.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: 5 to 35 °C. Storage below 0 °C or greater than 40 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact your local Henkel representative.
Parameters:
  • Chemical type : polyurea
  • Appearance (resin) : black liquid
  • Appearance (hardener) Opaque straw : yellow liquid
  • Appearance (mixed) : Black paste
  • Components Two components – resin & hardener
  • Mix Ratio, by weight - Resin : Hardener : 100 : 56
  • Application Temperature : 10°C to 30˚C (50°F to 86°F)
  • Mix Ratio, by volume - Resin : Hardener : 100 : 50
  • Cure : Room temperature cure after mixing
  • Application : Rubber repairs
  • Specific Benefits:
    - Resurfacing and repairing of worn or damaged rubber parts
    - Flexible
    - Fast curing
    - Application on vertical position
    - High abrasion resistance

    Further information can be found in the technical data sheet