LOCTITE UK 8160/UK 5400 - 3,6kg set (2C-polyurethane adhesive, up to 80 °C)
No.
IDH.80080
Files to download:
- Karta Techniczna - LOCTITE UK 8160 / LOCTITE UK 5400
- Technical Data Sheet - LOCTITE UK 8160 / LOCTITE UK 5400
- Technisches Datenblatt - LOCTITE UK 8160 / LOCTITE UK 5400
- Karta Charakterystyki (Składnik A) - LOCTITE UK 8160
- Karta Charakterystyki (Składnik B) - LOCTITE UK 5400
- Certyfikat DNVH (Odporność na ogień / Fire resistance)
LOCTITE UK 8160/UK 5400 - 3,6kg set (2C-polyurethane adhesive, up to 80 °C)
Product description:
LOCTITE UK 8160 / LOCTITE UK 5400 is a solvent-free two-component adhesive, based on polyurethane. The resin part (component A) contains organic compounds with hydroxyl groups, the hardener (component B) is based on isocyanates. By mixing both components in a mix ratio of 5 : 1 a hard elastic product is formed through chemical reaction. After curing the product exhibits no measurable change in volume. As natural raw materials (from different cultivation areas) are used a variation in color between different batches is possible. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Pretreatment
The substrate should be clean, dry, free of dust, oil, grease and other contaminants. The usage of suitable primers onmetal surfaces can improve the adhesion and/or the long-term bond stability. The surface of plastic materialsshould be cleaned, so as to remove any kind of release agents present on the substrate surface. An improvement ofthe adhesion can be achieved by grinding or sandblasting the surface.
Application
Adhesive components can be mixed manually, with stirring application or two-component mixing equipment. The product may be applied by spatula, wheel, pouring or spraying. The adhesive is only to be used within a limited time (pot life). After this time the mixture gels up and is not suitable for use. Therefore only the amount that can be applied within the time of pot life should be mixed. The pot life depends on the quantity and temperature of the mixed batch. With larger quantities and an increase in temperature, the pot life decreases. Lower temperatures extend the pot life. Adhesive components should not come into contact with moisture during storage or application. Contact with moisture (water vapour) generates foaming of the adhesive and weakens the bondline. Therefore all packaging should be sealed properly and protected against humidity during storage.
Curing
LOCTITE UK 8160 / LOCTITE UK 5400 can be cured at room temperature above 15°C and elevated temperatures (up to 60°C). The curing time can be reduced by increasing the temperature or the addition of the accelerator Loctite UK 6100, with the simultaneous reduction of processing time (i.e. pot life, open time) to be observed. While curing there should be adequate contact pressure (load pile, presses, clamps) and fixture hold the joint in place. An adhesive squeeze out along the bond line is a good indication of sufficient adhesive in the joints.
Storage:
Component A:Recommended Storage Temperature, °C : 15 to 30 Shelf-life (in unopened original packaging) : 12 monthsComponent B: Recommended Storage Temperature, °C : 15 to 30 Shelf-life (in unopened original packaging) : 12 months
Parameters:
Full technical information can be found in the technical data sheet.
LOCTITE UK 8160 / LOCTITE UK 5400 is a solvent-free two-component adhesive, based on polyurethane. The resin part (component A) contains organic compounds with hydroxyl groups, the hardener (component B) is based on isocyanates. By mixing both components in a mix ratio of 5 : 1 a hard elastic product is formed through chemical reaction. After curing the product exhibits no measurable change in volume. As natural raw materials (from different cultivation areas) are used a variation in color between different batches is possible. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
Pretreatment
The substrate should be clean, dry, free of dust, oil, grease and other contaminants. The usage of suitable primers onmetal surfaces can improve the adhesion and/or the long-term bond stability. The surface of plastic materialsshould be cleaned, so as to remove any kind of release agents present on the substrate surface. An improvement ofthe adhesion can be achieved by grinding or sandblasting the surface.
Application
Adhesive components can be mixed manually, with stirring application or two-component mixing equipment. The product may be applied by spatula, wheel, pouring or spraying. The adhesive is only to be used within a limited time (pot life). After this time the mixture gels up and is not suitable for use. Therefore only the amount that can be applied within the time of pot life should be mixed. The pot life depends on the quantity and temperature of the mixed batch. With larger quantities and an increase in temperature, the pot life decreases. Lower temperatures extend the pot life. Adhesive components should not come into contact with moisture during storage or application. Contact with moisture (water vapour) generates foaming of the adhesive and weakens the bondline. Therefore all packaging should be sealed properly and protected against humidity during storage.
Curing
LOCTITE UK 8160 / LOCTITE UK 5400 can be cured at room temperature above 15°C and elevated temperatures (up to 60°C). The curing time can be reduced by increasing the temperature or the addition of the accelerator Loctite UK 6100, with the simultaneous reduction of processing time (i.e. pot life, open time) to be observed. While curing there should be adequate contact pressure (load pile, presses, clamps) and fixture hold the joint in place. An adhesive squeeze out along the bond line is a good indication of sufficient adhesive in the joints.
Storage:
Component A:
Parameters:
- Density : approx. 1.45 g/cm 3
- Consistency: paste
- Pot life : 60 - 90 min
- Initial strength : after 5 - 8 hours
- Final strength : 5-7 days
- Working strength : after 24 hours in room temperature
- Shear strength:
- After 1 day : 5 MPa
- After 2 days : 7 MPa
- After 4 days : 8 MPa
- After 7 days : 10 MPa
- Color : beige
Full technical information can be found in the technical data sheet.