Product description:
LOCTITE EA 9464 is a faster cure version of LOCTITE EA 9461. The fixture time and pot life are reduced by approximately 50% while maintaining most of the performance of LOCTITE EA 9461. LOCTITE EA 9464 will achieve handling strength in 3 to 4 hours at room temperature (note: this can vary with different bond configurations and ambient temperatures). Elevated temperatures may be used to accelerate the cure. Further information about the product: biuro@woronko-kleje.pl

Steps to achieve the best adhesive results:
1. For best performance surfaces for bonding should be clean, dry and free of grease. You can use LOCTITE SF 7063 For high strength structural bonds, special surface treatments can increase the bond strength and durability.
2. To use, resin and hardener must be blended. Product can be applied directly from dual cartridges by dispensing through the mixer head supplied. Discard the first 3 to 5 cm of bead dispensed. Using bulk containers, mix thoroughly by weight or volume in the proportions specified in the Product Description Matrix. For hand mixing, weigh or measure out the desired amount of resin and hardener and mix thoroughly. Mix approximately 15 seconds after uniform color is obtained.
3. It is recommended that this product is not mixed and cured in bulk quantities of greater than 1 kg as excessive heat build-up can occur. Mixing smaller quantities will minimize the heat build-up.
4. Apply the adhesive as quickly as possible after mixing to one surface to be joined. For maximum bond strength apply adhesive evenly to both surfaces. Parts should be assembled immediately after mixed adhesive has been applied.
5. For working life please see section 'Typical Properties of Uncured Material'. Higher temperatures and larger quantities will shorten this working time.
6. Keep the assembled parts from moving during cure. The joint should be allowed to develop full strength beforesubjecting to any service loads.
7. Excess uncured adhesive can be wiped away with organic solvent (e.g. Acetone).
8. After use and before adhesive hardens, mixing and application equipment should be cleaned with hot soapy water.

Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Parameters:

Resin:
-Chemical type : epoxy
-Appearance: white no-transparent paste
-Degree of thixotropy: 2
-Flash point (TCC), °C (°F): >93(>200)

Hardener:
-Chemical type: amine
-Appearance: black no-transparent paste
-Specific gravity at 25°C: 1,31
-Degree of thixotropy: 1,5
-Flash point (TCC), °C (°F): >93(>200)

Adhesive after mixing ingredients:
-Appearance: grey no-transparent paste
-Mixing ratio by volume (resin / hardener): 1:1
-Mixing ratio by weight (resin / hardener): 100:100
-Viscosity, mPas: 150,000-250,000
-Maximum gap (mm): 3
-The shelf life of the mixed adhesive in 22 °C (100 g): 15-20
-Fixing time (light loads, 0,1 N/mm²) in 22°C, minutes: 180

Shear strength (7 days at 23°C, gap 0,05 mm) :
  • Steel (shot-blasted): 22 N/mm²
  • Aluminum (abraded): 18,2 N/mm²
  • Aluminum (etched): 22,1 N/mm²
  • Stainless steel: 18,4 N/mm²
  • Brass: 9,1 N/mm²
  • Zinc coating: 15,1 N/mm²
  • Galvanized steel: 20 N/mm²
  • Polycarbonate: 3,8 N/mm²
  • ABS: 4,8 N/mm²
  • GRP: 4,7 N/mm²

Full technical information can be found in the technical data sheet.