LOCTITE SI 5910 BK - 80ml Quick Gasket (oil-resistant silicone for sealing metal flanges, black)
No.
IDH.2394516
Associated products:
- LOCTITE SI 5910 BK - 50ml Quick Gasket (oil-resistant silicone for sealing metal flanges, black) (IDH.2394515)
- LOCTITE SF 7063 - 400ml (degreasing agent for plastics and metals) spray (IDH.2385316)
- LOCTITE SI 5910 BK - 100ml Quick Gasket (oil-resistant silicone for sealing metal flanges, black) (IDH.2325872)
LOCTITE SI 5910 BK - 80ml Quick Gasket (oil-resistant silicone for sealing metal flanges, black)
Associated products:
- LOCTITE SI 5910 BK - 50ml Quick Gasket (oil-resistant silicone for sealing metal flanges, black) (IDH.2394515)
- LOCTITE SF 7063 - 400ml (degreasing agent for plastics and metals) spray (IDH.2385316)
- LOCTITE SI 5910 BK - 100ml Quick Gasket (oil-resistant silicone for sealing metal flanges, black) (IDH.2325872)
Product description:
Typical applications include stamped sheet metal covers (timing covers and oil sumps) where good oil resistance andthe ability to withstand high joint-movement is required. The thixotropic nature of LOCTITE SI 5910 reduces the migration of liquid product after application to the substrate. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. Use LOCTITE SF 7063.
2. Moisture curing begins immediately after the product is exposed to the atmosphere, therefore parts to be assembled should be mated within a few minutes after the product is dispensed.
3. The bond should be allowed to cure (e.g. seven days), before subjecting to heavy service loads.
4. Excess material can be easily wiped away with non-polar solvents.
5. For full automatic applications a volumetric dispensing system is recommended.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
Full technical information can be found in the technical data sheet.
Typical applications include stamped sheet metal covers (timing covers and oil sumps) where good oil resistance andthe ability to withstand high joint-movement is required. The thixotropic nature of LOCTITE SI 5910 reduces the migration of liquid product after application to the substrate. Further information about the product: biuro@woronko-kleje.pl
Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. Use LOCTITE SF 7063.
2. Moisture curing begins immediately after the product is exposed to the atmosphere, therefore parts to be assembled should be mated within a few minutes after the product is dispensed.
3. The bond should be allowed to cure (e.g. seven days), before subjecting to heavy service loads.
4. Excess material can be easily wiped away with non-polar solvents.
5. For full automatic applications a volumetric dispensing system is recommended.
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
- Shear strength ( after 21 days at the temperature 23 °C / 60±5% RH and 0,5 mm gap) :
-Aluminum : 1 N/mm²
-Zinc dichromate : 1,4 N/mm²
-Dural : 1,4 N/mm² - Working temperature : from -55 °C to +200 °C
- Shore Hardness : 30 Shore A
- Color : black
- Elongation at break : 550%
Full technical information can be found in the technical data sheet.